| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | |||
| Viscosity | 38000 cP | 38000 cP | Mixed Viscosity | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 78 | 78 | |||
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D790 | ||
| Shear Strength | 32.9 MPa | 4770 psi | ASTM D1002-94 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 3.00e+13 ohm-cm | 3.00e+13 ohm-cm | |||
| Dielectric Constant | 4.28 @Frequency 1000 Hz | 4.28 @Frequency 1000 Hz | |||
| Dielectric Strength | 16.1 kV/mm | 410 kV/in | |||
| Dissipation Factor | 0.40 | 0.40 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 77.4 µm/m-°C @Temperature 20.0 °C | 43.0 µin/in-°F @Temperature 68.0 °F | |||
| Maximum Service Temperature, Air | 163 °C | 325 °F | |||
| Minimum Service Temperature, Air | -55.0 °C | -67.0 °F | |||
| Shrinkage | 0.10 % | 0.10 % | Cure Shrinkage | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min | 2.00 hour | at 150°F (Recommended Cure) | ||
| 2880 min | 48.0 hour | Room Temperature (Alternate Cure) | |||
| Pot Life | 45 min | 45 min | 100 gm mass @ 25°C | ||
| Descriptive Properties | |||||
| Chemical Resistance | Good | ||||
| Mix Ratio by Weight | 1:1 | resin:hardener | |||