- 弯曲强度 [MPa]: 31.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.72 g/cc | 1.72 g/cc | |||
| Brookfield Viscosity | 3800 cP @Temperature 23.9 °C | 3800 cP @Temperature 75.0 °F | Mixed | ||
| Linear Mold Shrinkage | 0.0027 cm/cm | 0.0027 in/in | ASTM D2566-69 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 85 @Temperature 23.9 °C | 85 @Temperature 75.0 °F | |||
| Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | |||
| Flexural Strength | 49.6 MPa | 7200 psi | |||
| Compressive Strength | 75.8 MPa | 11000 psi | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 75.6 µm/m-°C | 42.0 µin/in-°F | |||
| Heat Distortion Temperature | 52.8 °C | 127 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | >= 2880 min @Temperature 24.0 °C | >= 48.0 hour @Temperature 75.2 °F | |||
| Pot Life | >= 240 min @Temperature 24.0 °C | >= 240 min @Temperature 75.2 °F | 2 lb. mass | ||
| Descriptive Properties | |||||
| Machinability | Excellent | ||||
| Mix Ratio | 6:1 by weight, 2.9:1 by volume, resin/harder | ||||