- 弯曲强度 [MPa]: 53.8
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.69 g/cc | 1.69 g/cc | |||
| Brookfield Viscosity | 15000 cP @Temperature 23.9 °C | 15000 cP @Temperature 75.0 °F | Mixed | ||
| Linear Mold Shrinkage | 0.0011 cm/cm | 0.0011 in/in | ASTM D2566-69 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 90 @Temperature 23.9 °C | 90 @Temperature 75.0 °F | |||
| Tensile Strength, Ultimate | 53.8 MPa | 7800 psi | |||
| Flexural Strength | 59.3 MPa | 8600 psi | |||
| Compressive Strength | 200 MPa | 29000 psi | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 34.2 µm/m-°C | 19.0 µin/in-°F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 305 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 1440 min @Temperature 24.0 °C | 24.0 hour @Temperature 75.2 °F | |||
| Pot Life | 85 min @Temperature 24.0 °C | 85 min @Temperature 75.2 °F | 1 lb. mass | ||
| Descriptive Properties | |||||
| Mix Ratio | 100:7 by weight, 100:12 by volume, resin/harder | ||||