- 弯曲强度 [MPa]: 200.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | |||
| Brookfield Viscosity | 2000 cP @Temperature 23.9 °C | 2000 cP @Temperature 75.0 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 90 @Temperature 23.9 °C | 90 @Temperature 75.0 °F | |||
| Tensile Strength, Ultimate | 200 MPa | 29000 psi | 10 oz glass cloth laminate | ||
| Flexural Strength | 234 MPa | 34000 psi | 10 oz glass cloth laminate | ||
| Compressive Strength | 404 MPa | 58600 psi | 10 oz glass cloth laminate | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 16.2 µm/m-°C | 9.00 µin/in-°F | 10 oz glass cloth laminate | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 1440 min @Temperature 24.0 °C | 24.0 hour @Temperature 75.2 °F | |||
| Pot Life | 55 min @Temperature 24.0 °C | 55 min @Temperature 75.2 °F | |||
| Descriptive Properties | |||||
| Mix Ratio | 100:17 by weight, 100:20 by volume, resin/harder | ||||