- 弯曲强度 [MPa]: 37.2
- 弯曲模量 [MPa]: 5.58
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 2.27 g/cc | 2.27 g/cc | |||
| Brookfield Viscosity | 35000 cP @Temperature 23.9 °C | 35000 cP @Temperature 75.0 °F | Mixed | ||
| Linear Mold Shrinkage | 0.00090 cm/cm | 0.00090 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 85 @Temperature 23.9 °C | 85 @Temperature 75.0 °F | |||
| Tensile Strength, Ultimate | 37.2 MPa | 5400 psi | |||
| Flexural Strength | 51.0 MPa | 7400 psi | |||
| Flexural Modulus | 5.58 GPa | 810 ksi | |||
| Compressive Strength | 86.9 MPa | 12600 psi | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 50.6 °C | 123 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 1440 min @Temperature 24.0 °C | 24.0 hour @Temperature 75.2 °F | |||
| Pot Life | 240 min @Temperature 24.0 °C | 240 min @Temperature 75.2 °F | 15 lb. mass | ||
| Descriptive Properties | |||||
| Machinability | Good | ||||
| Mix Ratio | 12:1 by weight, 4.5:1 by volume, resin/harder | ||||