- 密度 [g/cm3]: 1.275
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.275 g/cc | 0.04606 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 38.1 microns | 1.50 mil | Side 1; Arlon SQA-TMS-003 | ||
| 38.1 microns | 1.50 mil | Side 2; Arlon SQA-TMS-003 | |||
| 203 microns | 8.00 mil | Substrate; Arlon SQA-TMS-003 | |||
| 279 microns | 11.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 83 | 83 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 7.329 MPa | 1063 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 134 % | 134 % | Silicone Property; ASTM D412 | ||
| Shear Strength | 2.76 MPa | 400 psi | ASTM D1002 | ||
| Tear Strength | 25.2 kN/m | 144 pli | Die B, Silicone Property; ASTM D624 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 31.5 kV/mm | 800 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | ||
| Shelf Life | 6.00 Month @Temperature 1.67 - 7.22 °C | 6.00 Month @Temperature 35.0 - 45.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Red | ||||
| Red | Substrate | ||||
| Total Product Weight (oz/yd2) | 11.8 | Arlon SQA-TMS-025 | |||
| Uncoated Fabric Break Strength | 345 lbf/in | Fill Strength, Arlon SQA-TMS-027 | |||
| 409 lbf/in | Warp Strength, Arlon SQA-TMS-027 | ||||