- 密度 [g/cm3]: 1.75
- 吸水率 [%]: 0.05
- 缺口冲击强度: 0.59
- 弯曲模量 [MPa]: 13.8
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.800 g/cc | 0.0289 lb/in³ | ASTM D1895 | ||
| Density | 1.75 g/cc | 0.0632 lb/in³ | ASTM D792 | ||
| Water Absorption | 0.050 % @Time 86400 sec | 0.050 % @Time 24.0 hour | ASTM D570 | ||
| 0.30 % @Time 173000 sec | 0.30 % @Time 48.0 hour | ASTM D570 | |||
| Linear Mold Shrinkage | 0.0015 cm/cm | 0.0015 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell E | 85 | 85 | ASTM D785 | ||
| Tensile Strength at Break | 96.0 MPa | 13900 psi | ASTM D638 | ||
| Flexural Strength | 186 MPa | 27000 psi | ASTM D790 | ||
| Flexural Modulus | 13.8 GPa | 2000 ksi | ASTM D790 | ||
| Compressive Strength | 234 MPa | 33900 psi | ASTM D695 | ||
| Izod Impact, Notched | 0.590 J/cm | 1.11 ft-lb/in | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 11.4 kV/mm @Frequency 60.0 Hz | 290 kV/in @Frequency 60.0 Hz | step-by-step, wet; ASTM D149 | ||
| 13.8 kV/mm @Frequency 60.0 Hz | 351 kV/in @Frequency 60.0 Hz | short time, wet; ASTM D149 | |||
| Arc Resistance | 135 sec | 135 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 13.0 µm/m-°C | 7.22 µin/in-°F | ASTM E831 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | As Molded; ASTM D648A | ||
| >= 282 °C | >= 540 °F | Post Baked; ASTM D648A | |||
| Descriptive Properties | |||||
| Color | Black | ||||
| Form | Granular | ||||
| Molding Method | Compression | ||||
| Injection | |||||
| Transfer | |||||