- 密度 [g/cm3]: 1.83
- 吸水率 [%]: 0.07
- 缺口冲击强度: 0.22
- 弯曲强度 [MPa]: 48.0
- 弯曲模量 [MPa]: 14.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.750 g/cc | 0.0271 lb/in³ | Powder; ASTM D1895 | ||
| Density | 1.83 g/cc | 0.0661 lb/in³ | ASTM D-792 | ||
| Water Absorption | 0.070 % | 0.070 % | 24 hour; ASTM D570 | ||
| 0.20 % | 0.20 % | 48 hour; ASTM D570 | |||
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell E | 90 | 90 | ASTM D785 | ||
| Tensile Strength, Ultimate | 48.0 MPa | 6960 psi | ASTM D638 | ||
| Flexural Strength | 105 MPa | 15200 psi | ASTM D790 | ||
| Flexural Modulus | 14.0 GPa | 2030 ksi | ASTM D790 | ||
| Compressive Strength | 210 MPa | 30500 psi | ASTM D695 | ||
| Izod Impact, Notched | 0.220 J/cm | 0.412 ft-lb/in | ASTM D256A | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 29.0 µm/m-°C @Temperature 20.0 °C | 16.1 µin/in-°F @Temperature 68.0 °F | ASTM E831 | ||
| Thermal Conductivity | 0.750 W/m-K | 5.20 BTU-in/hr-ft²-°F | ASTM C518 | ||
| Maximum Service Temperature, Air | 150 °C | 302 °F | UL Temperature Index; UL 746B | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | As Molded; ASTM D648A | ||
| >= 282 °C | >= 540 °F | Post Baked; ASTM D648A | |||
| Flammability, UL94 | V-0 @Thickness 3.20 mm | V-0 @Thickness 0.126 in | |||
| Descriptive Properties | |||||
| Available Molding Grades | Compression, Transfer, Injection | ||||
| Color | Black | ||||
| Form | Granular | ||||