- 密度 [g/cm3]: 1.78
- 吸水率 [%]: 0.07
- 缺口冲击强度: 0.26
- 弯曲强度 [MPa]: 34.0
- 弯曲模量 [MPa]: 13.8
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.750 g/cc | 0.0271 lb/in³ | Powder; ASTM D1895 | ||
| Density | 1.78 g/cc | 0.0643 lb/in³ | ASTM D-792 | ||
| Water Absorption | 0.070 % | 0.070 % | 24 hour; ASTM D570 | ||
| 0.20 % | 0.20 % | 48 hour; ASTM D570 | |||
| Linear Mold Shrinkage | 0.0015 - 0.0030 cm/cm | 0.0015 - 0.0030 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 34.0 MPa | 4930 psi | ASTM D638 | ||
| Flexural Strength | 75.0 MPa | 10900 psi | ASTM D790 | ||
| Flexural Modulus | 13.8 GPa | 2000 ksi | ASTM D790 | ||
| Compressive Strength | 137 MPa | 19900 psi | ASTM D695 | ||
| Izod Impact, Notched | 0.260 J/cm | 0.487 ft-lb/in | ASTM D256A | ||
| Thermal Properties | Metric | English | Comments | ||
| Thermal Conductivity | 1.22 W/m-K | 8.47 BTU-in/hr-ft²-°F | ASTM C518 | ||
| Maximum Service Temperature, Air | 150 °C | 302 °F | UL Temperature Index; UL 746B | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 191 °C | 376 °F | As Molded; ASTM D648A | ||
| >= 282 °C | >= 540 °F | Post Baked; ASTM D648A | |||
| Flammability, UL94 | V-0 @Thickness 3.20 mm | V-0 @Thickness 0.126 in | |||
| Descriptive Properties | |||||
| Available Molding Grades | Compression, Transfer, Injection | ||||
| Color | Black | ||||
| Form | Granular | ||||