- 密度 [g/cm3]: 1.45
- 吸水率 [%]: 0.9
- 弯曲模量 [MPa]: 23.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.500 g/cc | 0.0181 lb/in³ | ISO 60 | ||
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.90 % | 0.90 % | ISO 62 | ||
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell E | 100 | 100 | ISO 2039/2 | ||
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527 | ||
| Flexural Strength | 245 MPa | 35500 psi | ISO 178 | ||
| Flexural Modulus | 23.0 GPa | 3340 ksi | ISO 178 | ||
| Compressive Strength | 320 MPa | 46400 psi | ISO 604 | ||
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C | 5.56 µin/in-°F | ASTM E831 | ||
| CTE, linear, Transverse to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ASTM E831 | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| Form | Pellet | ||||
| Molding Method | Compression | ||||
| Injection | |||||
| Transfer | |||||