- 密度 [g/cm3]: 1.8
- 吸水率 [%]: 0.05
- 弯曲强度 [MPa]: 90.0
- 弯曲模量 [MPa]: 19.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.800 g/cc | 0.0289 lb/in³ | Powder; ISO 60 | ||
| Density | 1.80 g/cc | 0.0650 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.050 % | 0.050 % | ISO 62 | ||
| Linear Mold Shrinkage | 0.0015 cm/cm | 0.0015 in/in | ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 100 | 100 | ISO 2039/2 | ||
| Tensile Strength, Ultimate | 90.0 MPa | 13100 psi | ISO 527 | ||
| Flexural Strength | 185 MPa | 26800 psi | ISO 178 | ||
| Flexural Modulus | 19.0 GPa | 2760 ksi | ISO 178 | ||
| Compressive Strength | 360 MPa | 52200 psi | ISO 604 | ||
| Charpy Impact, Notched | 0.450 J/cm² | 2.14 ft-lb/in² | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 12.0 kV/mm @Thickness 3.00 mm | 305 kV/in @Thickness 0.118 in | IEC 243 | ||
| Arc Resistance | 135 sec | 135 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 14.0 µm/m-°C @Temperature 23.0 °C | 7.78 µin/in-°F @Temperature 73.4 °F | TMA | ||
| Thermal Conductivity | 0.600 W/m-K | 4.16 BTU-in/hr-ft²-°F | ASTM F433 | ||
| Maximum Service Temperature, Air | 150 °C | 302 °F | UL Temperature Index; UL 746B | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | As Molded; ISO 75 A | ||
| >= 282 °C | >= 540 °F | Post Baked; ISO 75 A | |||
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |||
| V-0 @Thickness 3.20 mm | V-0 @Thickness 0.126 in | ||||
| Descriptive Properties | |||||
| Available Molding Grades | Compression, Transfer, Injection | ||||
| Color | Black, Green | ||||
| Form | Granular | ||||