- 密度 [g/cm3]: 0.128
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.128 g/cc | 0.00463 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Compressive Yield Strength | >= 6.89 MPa | >= 1000 psi | Bare, min |
| >= 8.14 MPa | >= 1180 psi | Stabilized, min | |
| 9.65 MPa | 1400 psi | Bare, typ | |
| 10.6 MPa | 1540 psi | Stabilized, typ | |
| Compressive Modulus | 1.03 GPa | 150 ksi | Stabilized, typ |
| Shear Modulus | 0.124 GPa | 18.0 ksi | Plate Shear, W Direction, typ |
| 0.186 GPa | 27.0 ksi | Plate Shear, L Direction, typ | |
| Shear Strength | >= 2.41 MPa | >= 350 psi | Plate Shear, W Direction, min |
| 3.10 MPa | 450 psi | Plate Shear, W Direction, typ | |
| >= 3.72 MPa | >= 540 psi | Plate Shear, L Direction, min | |
| 4.83 MPa | 700 psi | Plate Shear, L Direction, typ | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 177 °C | 350 °F | High strength retained |