- 弯曲强度 [MPa]: 21.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 26 @Temperature 121 °C | 26 @Temperature 250 °F | ML-10 (gum) |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 71 | 71 | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Elongation at Break | 230 % | 230 % | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Modulus of Elasticity | 0.000700 GPa | 0.102 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| 100% Modulus | 0.00530 GPa | 0.769 ksi | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
| Compression Set | 32 % @Temperature 200 °C | 32 % @Temperature 392 °F | Method B, O-rings 22 hr at 200°C (Post Cured 16 hr at 232°C) |
| Thermal Properties | Metric | English | Comments |
| Glass Transition Temp, Tg | -17.9 °C | -0.220 °F | DSC, modulated, midpoint |