- 透光率 [%]: 25.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Mooney Viscosity | 80 @Temperature 121 °C | 80 @Temperature 250 °F | ML 1+10 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 60 | 60 | Press Cure 10 Minutes @ 165°C (350°F) Ramp Post Cure in Air; ASTM D2240 | ||
| 56 @Time 86400 sec | 56 @Time 24.0 hour | Press Cure 10 Minutes @ 165°C (330°F) Ramp Post Cure in Air, Time Held at 300°C (572°F); ASTM D2240 | |||
| 57 @Time 14400 sec | 57 @Time 4.00 hour | Press Cure 10 Minutes @ 165°C (330°F) Ramp Post Cure in Air, Time Held at 300°C (572°F); ASTM D2240 | |||
| Tensile Strength at Break | 13.2 MPa @Time 86400 sec | 1910 psi @Time 24.0 hour | Press Cure 10 Minutes @ 165°C (330°F) Ramp Post Cure in Air, Time Held at 300°C (572°F); ASTM D412 Die D Dumbbells | ||
| 13.8 MPa @Time 14400 sec | 2000 psi @Time 4.00 hour | Press Cure 10 Minutes @ 165°C (330°F) Ramp Post Cure in Air, Time Held at 300°C (572°F); ASTM D412 Die D Dumbbells | |||
| Elongation at Break | 295 % | 295 % | Press Cure 10 Minutes @ 165°C (350°F) Ramp Post Cure in Air; ASTM D412 Die D Dumbbells | ||
| 275 % @Time 86400 sec | 275 % @Time 24.0 hour | Press Cure 10 Minutes @ 165°C (330°F) Ramp Post Cure in Air, Time Held at 300°C (572°F); ASTM D412 Die D Dumbbells | |||
| 295 % @Time 14400 sec | 295 % @Time 4.00 hour | Press Cure 10 Minutes @ 165°C (330°F) Ramp Post Cure in Air, Time Held at 300°C (572°F); ASTM D412 Die D Dumbbells | |||
| 100% Modulus | 0.00120 GPa @Time 86400 sec | 0.174 ksi @Time 24.0 hour | Press Cure 10 Minutes @ 165°C (330°F) Ramp Post Cure in Air, Time Held at 300°C (572°F); ASTM D412 Die D Dumbbells | ||
| 0.00130 GPa @Time 14400 sec | 0.189 ksi @Time 4.00 hour | Press Cure 10 Minutes @ 165°C (330°F) Ramp Post Cure in Air, Time Held at 300°C (572°F); ASTM D412 Die D Dumbbells | |||
| Compression Set | 8.0 % @Treatment Temp. 200 °C, Time 79200 sec | 8.0 % @Treatment Temp. 392 °F, Time 22.0 hour | Method B, -214 O-rings, Press Cure 10 Minutes @ 165°C Ramp Post Cure in Air; ASTM D395 | ||
| 15 % @Treatment Temp. 250 °C, Time 79200 sec | 15 % @Treatment Temp. 482 °F, Time 22.0 hour | Method B, -214 O-rings, Press Cure 10 Minutes @ 165°C Ramp Post Cure in Air; ASTM D395 | |||
| 16 % @Treatment Temp. 200 °C, Time 252000 sec | 16 % @Treatment Temp. 392 °F, Time 70.0 hour | Method B, -214 O-rings, Press Cure 10 Minutes @ 165°C Ramp Post Cure in Air; ASTM D395 | |||
| 19 % @Treatment Temp. 250 °C, Time 252000 sec | 19 % @Treatment Temp. 482 °F, Time 70.0 hour | Method B, -214 O-rings, Press Cure 10 Minutes @ 165°C Ramp Post Cure in Air; ASTM D395 | |||
| 19 % @Treatment Temp. 250 °C, Time 252000 sec | 19 % @Treatment Temp. 482 °F, Time 70.0 hour | 4 hrs, Method B, -214 O-rings; ASTM D395 | |||
| 20 % @Treatment Temp. 250 °C, Time 252000 sec | 20 % @Treatment Temp. 482 °F, Time 70.0 hour | 4 hrs, Method B, -214 O-rings; ASTM D395 | |||
| 20 % @Treatment Temp. 200 °C, Time 605000 sec | 20 % @Treatment Temp. 392 °F, Time 168 hour | Method B, -214 O-rings, Press Cure 10 Minutes @ 165°C Ramp Post Cure in Air; ASTM D395 | |||
| 22 % @Treatment Temp. 250 °C, Time 605000 sec | 22 % @Treatment Temp. 482 °F, Time 168 hour | 24 hrs, Method B, -214 O-rings; ASTM D395 | |||
| 24 % @Treatment Temp. 250 °C, Time 605000 sec | 24 % @Treatment Temp. 482 °F, Time 168 hour | Method B, -214 O-rings, Press Cure 10 Minutes @ 165°C Ramp Post Cure in Air; ASTM D395 | |||
| 24 % @Treatment Temp. 250 °C, Time 605000 sec | 24 % @Treatment Temp. 482 °F, Time 168 hour | 24 hrs, Method B, -214 O-rings; ASTM D395 | |||
| 25 % @Treatment Temp. 200 °C, Time 1.21e+6 sec | 25 % @Treatment Temp. 392 °F, Time 336 hour | Method B, -214 O-rings, Press Cure 10 Minutes @ 165°C Ramp Post Cure in Air; ASTM D395 | |||
| 26 % @Treatment Temp. 275 °C, Time 79200 sec | 26 % @Treatment Temp. 527 °F, Time 22.0 hour | Method B, -214 O-rings, Press Cure 10 Minutes @ 165°C Ramp Post Cure in Air; ASTM D395 | |||
| 28 % @Treatment Temp. 250 °C, Time 1.21e+6 sec | 28 % @Treatment Temp. 482 °F, Time 336 hour | Method B, -214 O-rings, Press Cure 10 Minutes @ 165°C Ramp Post Cure in Air; ASTM D395 | |||
| 33 % @Treatment Temp. 275 °C, Time 252000 sec | 33 % @Treatment Temp. 527 °F, Time 70.0 hour | Method B, -214 O-rings, Press Cure 10 Minutes @ 165°C Ramp Post Cure in Air; ASTM D395 | |||
| 36 % @Treatment Temp. 275 °C, Time 605000 sec | 36 % @Treatment Temp. 527 °F, Time 168 hour | Method B, -214 O-rings, Press Cure 10 Minutes @ 165°C Ramp Post Cure in Air; ASTM D395 | |||
| 53 % @Treatment Temp. 275 °C, Time 1.21e+6 sec | 53 % @Treatment Temp. 527 °F, Time 336 hour | Method B, -214 O-rings, Press Cure 10 Minutes @ 165°C Ramp Post Cure in Air; ASTM D395 | |||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | 25 % | 25 % | translucent, but thickness not quantified | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 50.0 - 70.0 °C | 122 - 158 °F | |||
| Die Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |||
| Head Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |||
| Screw Cooling Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Component Elements Properties | Metric | English | Comments | ||
| Fluorine, F | 72.4 % | 72.4 % | |||
| Descriptive Properties | |||||
| Color | Translucent, Clear-Amber | ||||
| Dry Heat Resistance of Vulcanizate - 100% Modulus | 1.103 MPa | 300°C; 336 hours | |||
| 1.13 MPa | 300°C; 168 hours | ||||
| 1.17 MPa | 300°C; 70 hours | ||||
| 1.62 MPa | 250°C; 70 hours | ||||
| 1.72 MPa | 200°C; 168 hours | ||||
| 1.75 MPa | 250°C; 336 hours | ||||
| 1.83 MPa | 200°C; 70 hours | ||||
| 1.86 MPa | 250°C; 168 hours | ||||
| 2.03 MPa | 200°C; 336 hours | ||||
| 275°C; 168 hours MPa | °C; hours | ||||
| 275°C; 70 hours MPa | °C; hours | ||||
| Dry Heat Resistance of Vulcanizate - Elongation | 250 percent | 275°C; 70 hours | |||
| 255 percent | 250°C; 168 hours | ||||
| 270 percent | 275°C; 168 hours | ||||
| 275 percent | 200°C; 168 hours | ||||
| 280 percent | 200°C; 336 hours | ||||
| 280 percent | 250°C; 70 hours | ||||
| 280 percent | 250°C; 336 hours | ||||
| 290 percent | 200°C; 70 hours | ||||
| 370 percent | 300°C; 70 hours | ||||
| 375 percent | 300°C; 168 hours | ||||
| 380 percent | 300°C; 336 hours | ||||
| Dry Heat Resistance of Vulcanizate - Shore A Hardness | 55 | 275°C; 70 hours | |||
| 55 | 275°C; 168 hours | ||||
| 56 | 300°C; 336 hours | ||||
| 57 | 300°C; 70 hours | ||||
| 57 | 300°C; 168 hours | ||||
| 60 | 250°C; 336 hours | ||||
| 60 | 250°C; 70 hours | ||||
| 61 | 250°C; 168 hours | ||||
| 63 | 200°C; 70 hours | ||||
| 64 | 200°C; 168 hours | ||||
| 65 | 200°C; 336 hours | ||||
| Dry Heat Resistance of Vulcanizate - Tensile Strength at Break | 10.89 MPa | 275°C; 168 hours | |||
| 11.51 MPa | 300°C; 336 hours | ||||
| 12.89 MPa | 300°C; 168 hours | ||||
| 12.96 MPa | 275°C; 70 hours | ||||
| 15.2 MPa | 300°C; 70 hours | ||||
| 16.89 MPa | 250°C; 336 hours | ||||
| 17.72 MPa | 250°C; 168 hours | ||||
| 18.34 MPa | 200°C; 70 hours | ||||
| 19.51 MPa | 250°C; 70 hours | ||||
| 19.96 MPa | 200°C; 168 hours | ||||
| 20.86 MPa | 200°C; 336 hours | ||||
| Form | Slab | ||||
| MH, Maximum Toque | 3.7 inch-lb | 100 cpm, 0.5° Arc, 10 Minutes @ 165°C | |||
| ML, Minimum Torque | 1.0 inch-lb | 100 cpm, 0.5° Arc, 10 Minutes @ 165°C | |||
| t2, Time to 2 Inch-lb Rise from Minimum | 3.2 Minute | 100 cpm, 0.5° Arc, 10 Minutes @ 165°C | |||
| t'50, Time to 50% Cure | 2.1 Minutes | 100 cpm, 0.5° Arc, 10 Minutes @ 165°C | |||
| t'90, Time to 90% Cure | 5.2 Minutes | 100 cpm, 0.5° Arc, 10 Minutes @ 165°C | |||