- 拉伸强度 [MPa]: 34.1
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 66 | 66 | |
| Tensile Strength, Yield | 34.1 MPa | 4940 psi | |
| Elongation at Yield | 620 % | 620 % | |
| 100% Modulus | 0.00317 GPa | 0.460 ksi | |
| 200% Modulus | 0.006998 GPa | 1.015 ksi | |
| 300% Modulus | 0.0125 GPa | 1.82 ksi | |
| Tear Strength | 64.5 kN/m | 368 pli | Die C |
| Compression Set | 31.5 % @Temperature 70.0 °C, Time 79200 sec | 31.5 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 3.00 min @Temperature 155 °C | 0.0500 hour @Temperature 311 °F | ts2 |
| 6.80 min @Temperature 155 °C | 0.113 hour @Temperature 311 °F | TC90 | |