- 拉伸强度 [MPa]: 33.5
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 70 | 70 | |
| Tensile Strength, Yield | 33.5 MPa | 4860 psi | |
| Elongation at Yield | 540 % | 540 % | |
| 100% Modulus | 0.00414 GPa | 0.600 ksi | |
| 200% Modulus | 0.009701 GPa | 1.407 ksi | |
| 300% Modulus | 0.01690 GPa | 2.451 ksi | |
| Tear Strength | 62.3 kN/m | 355 pli | Die C |
| Compression Set | 33.8 % @Temperature 70.0 °C, Time 79200 sec | 33.8 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 14.1 min @Temperature 155 °C | 0.235 hour @Temperature 311 °F | TC90 |