- 拉伸强度 [MPa]: 24.79
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 66 | 66 | |
| 70 | 70 | heat aged 70 hours @ 100ºC | |
| Tensile Strength, Yield | 24.79 MPa | 3596 psi | |
| 25.09 MPa | 3639 psi | heat aged 70 hours @ 100ºC | |
| Elongation at Yield | 246 % | 246 % | heat aged 70 hours @ 100ºC |
| 300 % | 300 % | ||
| 100% Modulus | 0.00451 GPa | 0.654 ksi | |
| 200% Modulus | 0.01531 GPa | 2.221 ksi | |
| 300% Modulus | 0.02468 GPa | 3.579 ksi | |
| Tear Strength | 50.1 kN/m | 286 pli | Die C |
| Compression Set | 25.7 % @Temperature 100 °C, Time 79200 sec | 25.7 % @Temperature 212 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 12.0 min @Temperature 83.3 °C | 0.200 hour @Temperature 182 °F | |