- 拉伸强度 [MPa]: 22.79
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 66 | 66 | |
| 70 | 70 | heat aged 70 hours @ 100ºC | |
| Tensile Strength, Yield | 22.79 MPa | 3305 psi | |
| 27.50 MPa | 3989 psi | heat aged 70 hours @ 100ºC | |
| Elongation at Yield | 256.336 % | 256.336 % | heat aged 70 hours @ 100ºC |
| 296 % | 296 % | ||
| 100% Modulus | 0.00405 GPa | 0.587 ksi | |
| 200% Modulus | 0.01364 GPa | 1.979 ksi | |
| Tear Strength | 52.4 kN/m | 299 pli | Die C |
| Compression Set | 24 % @Temperature 100 °C, Time 79200 sec | 24 % @Temperature 212 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 5.00 min @Temperature 83.3 °C | 0.0833 hour @Temperature 182 °F | |