- 拉伸强度 [MPa]: 33.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 70 | 70 | |
| Tensile Strength, Yield | 33.0 MPa | 4790 psi | |
| Elongation at Yield | 565 % | 565 % | |
| 100% Modulus | 0.00403 GPa | 0.585 ksi | |
| 200% Modulus | 0.00958 GPa | 1.39 ksi | |
| 300% Modulus | 0.0159 GPa | 2.31 ksi | |
| Tear Strength | 63.6 kN/m | 363 pli | Die C |
| Compression Set | 32.5 % @Temperature 70.0 °C, Time 79200 sec | 32.5 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 8.00 min @Temperature 155 °C | 0.133 hour @Temperature 311 °F | TC90 |