- 拉伸强度 [MPa]: 34.9
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 68 | 68 | |
| Tensile Strength, Yield | 34.9 MPa | 5060 psi | |
| Elongation at Yield | 590 % | 590 % | |
| 100% Modulus | 0.00365 GPa | 0.530 ksi | |
| 200% Modulus | 0.00841 GPa | 1.22 ksi | |
| 300% Modulus | 0.0148 GPa | 2.15 ksi | |
| Tear Strength | 66.5 kN/m | 379 pli | Die C |
| Compression Set | 32.5 % @Temperature 70.0 °C, Time 79200 sec | 32.5 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 3.50 min @Temperature 155 °C | 0.0583 hour @Temperature 311 °F | ts2 |
| 8.20 min @Temperature 155 °C | 0.137 hour @Temperature 311 °F | TC90 | |