- 拉伸强度 [MPa]: 32.62
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 71 | 71 | |
| Tensile Strength, Yield | 32.62 MPa | 4731 psi | |
| Elongation at Yield | 559 % | 559 % | |
| 100% Modulus | 0.00361 GPa | 0.524 ksi | |
| 200% Modulus | 0.008143 GPa | 1.181 ksi | |
| 300% Modulus | 0.01427 GPa | 2.069 ksi | |
| Tear Strength | 65.1 kN/m | 371 pli | Die C |
| Compression Set | 31.4 % @Temperature 70.0 °C, Time 79200 sec | 31.4 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 8.00 min @Temperature 155 °C | 0.133 hour @Temperature 311 °F | TC90 |