- 拉伸强度 [MPa]: 26.2142
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 64 | 64 | |
| 68 | 68 | heat aged 70 hours @ 100ºC | |
| Tensile Strength, Yield | 26.2142 MPa | 3802.05 psi | heat aged 70 hours @ 100ºC |
| 26.37 MPa | 3825 psi | ||
| Elongation at Yield | 282.88 % | 282.88 % | heat aged 70 hours @ 100ºC |
| 340 % | 340 % | ||
| 100% Modulus | 0.00442 GPa | 0.641 ksi | |
| 200% Modulus | 0.01451 GPa | 2.104 ksi | |
| 300% Modulus | 0.0235 GPa | 3.41 ksi | |
| Tear Strength | 59.0 kN/m | 337 pli | Die C |
| Compression Set | 25.9 % @Temperature 100 °C, Time 79200 sec | 25.9 % @Temperature 212 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 7.00 min @Temperature 83.3 °C | 0.117 hour @Temperature 182 °F | |