- 密度 [g/cm3]: 1.73
- 吸水率 [%]: 0.06
- 缺口冲击强度: 1.07
- 弯曲模量 [MPa]: 15.4
- 热变形温度 [℃]: 240.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.70 g/cc | 1.70 g/cc | ASTM D792 | ||
| Density | 1.73 g/cc | 0.0625 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.0600 % | 0.0600 % | 24hr immersion; ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.00200 cm/cm | 0.00200 in/in | ISO 294-4 | ||
| 0.00600 cm/cm | 0.00600 in/in | ASTM D955 | |||
| Linear Mold Shrinkage, Transverse | 0.00600 cm/cm | 0.00600 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 121 | 121 | ISO 2039-2 | ||
| Tensile Strength at Break | 174 MPa | 25200 psi | 5mm/min; ISO 527-2/1A | ||
| 197 MPa | 28500 psi | ASTM D638 | |||
| Elongation at Break | 1.70 % | 1.70 % | 5mm/min; ISO 527-2/1A | ||
| 2.00 % @Temperature 22.8 °C | 2.00 % @Temperature 73.0 °F | ASTM D638 | |||
| Tensile Modulus | 16.8 GPa | 2440 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 259 MPa | 37600 psi | ISO 178 | ||
| 292 MPa | 42400 psi | ASTM D790 | |||
| Flexural Modulus | 15.4 GPa | 2230 ksi | ISO 178 | ||
| 14.5 GPa @Temperature 22.8 °C | 2100 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 1.07 J/cm | 2.00 ft-lb/in | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 9.50 kJ/m² | 4.52 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact Unnotched | 2.40 J/cm² | 11.4 ft-lb/in² | ISO 179/1eU | ||
| 2.10 J/cm² @Temperature -30.0 °C | 9.99 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | ISO 179/1eA | ||
| 0.900 J/cm² @Temperature -30.0 °C | 4.28 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 | ||
| 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 | |||
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | ASTM D257 | ||
| Dielectric Constant | 3.40 @Frequency 1.00e+6 Hz | 3.40 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| 3.50 @Frequency 1000 Hz | 3.50 @Frequency 1000 Hz | ASTM D150 | |||
| 3.80 @Frequency 10000 Hz | 3.80 @Frequency 10000 Hz | ASTM D150 | |||
| Dielectric Strength | 21.3 kV/mm | 540 kV/in | short term; ASTM D149 | ||
| Dissipation Factor | 0.00600 @Frequency 1000 Hz | 0.00600 @Frequency 1000 Hz | ASTM D150 | ||
| 0.00900 @Frequency 10000 Hz | 0.00900 @Frequency 10000 Hz | ASTM D150 | |||
| 0.0120 @Frequency 1.00e+6 Hz | 0.0120 @Frequency 1.00e+6 Hz | ASTM D150 | |||
| Arc Resistance | 129 sec | 129 sec | ASTM D495 | ||
| Comparative Tracking Index | 225 V | 225 V | IEC 60112 | ||
| 250 V | 250 V | ASTM D3638 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 14.0 µm/m-°C | 7.78 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 83.0 µm/m-°C | 46.1 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 244 °C | 471 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Transformation Temperature, Tg | 73.0 °C | 163 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 229 °C | 444 °F | ISO 75-1, -2 | ||
| 229 °C | 445 °F | ASTM D648 | |||
| Flammability, UL94 | HB @Thickness 0.810 mm | HB @Thickness 0.0319 in | UL94 | ||
| Oxygen Index | 22.0 % | 22.0 % | ISO 4589 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| 110 - 121 °C | 230 - 250 °F | Cavity temperature | |||
| Feed Temperature | 255 - 265 °C | 491 - 509 °F | |||
| Rear Barrel Temperature | 260 - 270 °C | 500 - 518 °F | |||
| Middle Barrel Temperature | 270 - 275 °C | 518 - 527 °F | |||
| Front Barrel Temperature | 275 - 280 °C | 527 - 536 °F | |||
| Nozzle Temperature | 275 - 290 °C | 527 - 554 °F | |||
| Zone 1 | 255 - 265 °C | 491 - 509 °F | |||
| Zone 2 | 260 - 275 °C | 500 - 527 °F | |||
| Zone 3 | 260 - 275 °C | 500 - 527 °F | |||
| Zone 4 | 265 - 280 °C | 509 - 536 °F | |||
| Die Temperature | 270 - 290 °C | 518 - 554 °F | |||
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |||
| 270 - 300 °C | 518 - 572 °F | ||||
| 285 °C | 545 °F | Injection molding; ISO 294 | |||
| Mold Temperature | 110 - 121 °C | 230 - 250 °F | |||
| 135 °C | 275 °F | Injection molding; ISO 294 | |||
| Injection Velocity | 275 mm/sec | 10.8 in/sec | ISO 294 | ||
| Drying Temperature | 130 - 140 °C | 266 - 284 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | 0.0100 % | 0.0100 % | Necessary low maximum residual | ||
| Hold Pressure | 60.0 MPa | 8700 psi | ISO 294 | ||
| Back Pressure | 0.000 - 0.172 MPa | 0.000 - 25.0 psi | |||
| Screw Speed | 50.0 - 75.0 rpm | 50.0 - 75.0 rpm | |||
| Hot-Working Temperature | 260 - 290 °C | 500 - 554 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Longer pre-drying times/storage | 100° C | <= 60 h | |||
| Processing conditions | ISO 7792-2 | ||||
| Processing Notes | Medium/Fast Injection Speed | ||||