- 熔体流动速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.922
- 拉伸强度 [MPa]: 12.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | ISO 1183 |
| Melt Flow | 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.90 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Antiblock Level | 625 ppm | 625 ppm | Borealis Method |
| Slip Level | 480 ppm | 480 ppm | erucamide; Borealis Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 12.0 MPa | 1740 psi | MD/TD; ISO 527-3 |
| Film Elongation at Break, MD | 800 % | 800 % | ISO 527-3 |
| Film Elongation at Break, TD | 1000 % | 1000 % | ISO 527-3 |
| Tensile Modulus | 0.145 GPa | 21.0 ksi | MD; ASTM D882-A |
| 0.165 GPa | 23.9 ksi | TD; ASTM D882-A | |
| Coefficient of Friction | 0.10 | 0.10 | Dynamic; ISO 8295 |
| Elmendorf Tear Strength, MD | 2.91 g/micron | 73.9 g/mil | ISO 6383/2 |
| Elmendorf Tear Strength, TD | 13.11 g/micron | 333.0 g/mil | ISO 6383/2 |
| Dart drop Test | 260 g @Thickness 0.0700 mm | 0.573 lb @Thickness 0.00276 in | ISO 7765-1 |
| Film Tensile Strength at Break, MD | 29.0 MPa | 4210 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 28.0 MPa | 4060 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 122 °C | 252 °F | ISO 11357-3 |
| Optical Properties | Metric | English | Comments |
| Haze | 10 % | 10 % | ASTM D1003 |
| Gloss | 100 % | 100 % | ASTM D2457 |