- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D-1505 | ||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D-1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 600 % | 600 % | ASTM D-882 | ||
| Film Elongation at Break, TD | 700 % | 700 % | ASTM D-882 | ||
| Elmendorf Tear Strength MD | 105 g | 105 g | ASTM D-1922 | ||
| Elmendorf Tear Strength TD | 410 g | 410 g | ASTM D-1922 | ||
| Dart drop Test | 65.0 g | 0.143 lb | ASTM D-1709 | ||
| Film Tensile Strength at Break, MD | 27.0 MPa | 3920 psi | ASTM D-882 | ||
| Film Tensile Strength at Break, TD | 19.0 MPa | 2760 psi | ASTM D-882 | ||
| 1% Secant Modulus, MD | 172 MPa | 25000 psi | ASTM D-882 | ||
| 1% Secant Modulus, TD | 190 MPa | 27500 psi | ASTM D-882 | ||
| Descriptive Properties | |||||
| process | Film | ||||
| region | Europe/Turkey | ||||
| International | |||||
| Mexico | |||||
| US & Canada | |||||