- 熔体流动速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.956
- 拉伸强度 [MPa]: 22.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.956 g/cc | 0.0345 lb/in³ | Compound; ISO 1183 | ||
| Environmental Stress Crack Resistance | >= 2000 hour @Temperature 80.0 °C | >= 2000 hour @Temperature 176 °F | At 8.0 bar; ISO 13479 | ||
| Carbon Black Loading | >= 2.0 % | >= 2.0 % | ASTM D1603 | ||
| Melt Flow | 0.30 g/10 min @Load 5.00 kg, Temperature 190 °C | 0.30 g/10 min @Load 11.0 lb, Temperature 374 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | At 50 mm/min; ISO 527-2 | ||
| Elongation at Break | >= 600 % | >= 600 % | ISO 527-2 | ||
| Tensile Modulus | 1.00 GPa | 145 ksi | At 1 mm/min; ISO 527-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Die Temperature | 200 - 210 °C | 392 - 410 °F | |||
| Melt Temperature | 200 - 220 °C | 392 - 428 °F | |||
| Head Temperature | 200 - 210 °C | 392 - 410 °F | |||
| Descriptive Properties | |||||
| Resistance to Rapid Crack Propagation, BAR | 8 | ISO 13477, Pc at 0°C, S4 / pipe size 250 mm SDR 11 | |||