- 熔体流动速率 [g/10min]: 0.45
- 密度 [g/cm3]: 0.948
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.948 g/cc | 0.0342 lb/in³ | ASTM D1505 | ||
| Thickness | 38.0 microns | 1.50 mil | |||
| Melt Flow | 0.45 g/10 min @Load 5.00 kg, Temperature 190 °C | 0.45 g/10 min @Load 11.0 lb, Temperature 374 °F | ASTM D1238 | ||
| High Load Melt Index | 10 g/10 min @Load 21.6 kg, Temperature 190 °C | 10 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 23.0 MPa | 3340 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 27.0 MPa | 3920 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 571 % | 571 % | ASTM D882 | ||
| Film Elongation at Break, TD | 832 % | 832 % | ASTM D882 | ||
| Elmendorf Tear Strength, MD | 0.600 g/micron | 15.2 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 4.10 g/micron | 104 g/mil | ASTM D1922 | ||
| Dart Drop | 3.13 g/micron | 79.5 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 57.0 MPa | 8270 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 54.0 MPa | 7830 psi | ASTM D882 | ||
| Heat Seal Strength Initiation Temperature | 125 °C | 257 °F | Sealing Initial Temperature; Braskem® Method | ||
| Descriptive Properties | |||||
| Minimum Recommended Thickness | 13 µm | ||||
| Puncture Strength | 71 J/m | Braskem® Method | |||