- 熔体流动速率 [g/10min]: 7.0
- 密度 [g/cm3]: 0.957
- 缺口冲击强度: 0.55
- 拉伸强度 [MPa]: 26.0
- 弯曲模量 [MPa]: 1.30
- 热变形温度 [℃]: 71.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.957 g/cc | 0.0346 lb/in³ | ASTM D1505 |
| ESCR 100% Igepal® | 2.5 hour @Thickness 3.00 mm, Temperature 23.0 °C | 2.5 hour @Thickness 0.118 in, Temperature 73.4 °F | compression molded plaques; ASTM D1693B |
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 7.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638 |
| Flexural Modulus | 1.30 GPa | 189 ksi | ASTM D790 |
| Izod Impact, Notched | 0.550 J/cm | 1.03 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | ASTM D648 |
| Vicat Softening Point | 125 °C | 257 °F | ASTM D1525 |