- 密度 [g/cm3]: 1.14
- 拉伸强度 [MPa]: 59.0
- 弯曲强度 [MPa]: 45.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | (Dry) |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ASTM data at 5 mm/min. |
| Tensile Strength, Yield | 59.0 MPa | 8560 psi | ISO value at 50 mm/min. |
| 60.0 MPa | 8700 psi | ASTM value at 50 mm/min. | |
| Elongation at Break | >= 50 % | >= 50 % | Nominal strain at break, ISO, 50 mm/min |
| 70 % | 70 % | Strain at break, ASTM, 5 mm/min | |
| Elongation at Yield | 18 % | 18 % | ISO Value at 50 mm/min. |
| 20 % | 20 % | ASTM Value at 50 mm/min. | |
| Tensile Modulus | 1.70 GPa | 247 ksi | same value from ASTM and ISO test. |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | (Dry) |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 290 °C | 554 °F | See Materials Notes |
| Mold Temperature | 80.0 °C | 176 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |