- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 8.5
- 拉伸强度 [MPa]: 95.0
- 断裂伸长率 [%]: 135
- 弯曲模量 [MPa]: 3.36
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO data |
| Moisture Absorption at Equilibrium | 2.5 % | 2.5 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 8.5 % | 8.5 % | in water; 23°C; ISO data |
| Viscosity Measurement | 55 | 55 | Formic Acid Viscosity; ISO data |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | 50 mm/min; Same value from ASTM and ISO test. |
| Elongation at Break | 13 % | 13 % | Nominal strain at break, ISO, 50 mm/min |
| 15 % | 15 % | Nominal strain at break, ASTM, 50 mm/min | |
| Elongation at Yield | 4.0 % | 4.0 % | ISO Value at 50 mm/min. |
| 4.0 % | 4.0 % | ASTM Value at 50 mm/min. | |
| Tensile Modulus | 3.70 GPa | 537 ksi | same value from ASTM and ISO test. |
| Flexural Yield Strength | 135 MPa | 19600 psi | ASTM Data |
| Flexural Modulus | 3.36 GPa | 487 ksi | ASTM Data |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Shear Modulus | 1.40 GPa | 203 ksi | calculated |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ISO data |
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | ISO data |
| Comparative Tracking Index | 600 V | 600 V | ISO data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | ASTM and ISO test |
| Deflection Temperature at 1.8 MPa (264 psi) | 81.0 °C | 178 °F | ASTM Data |
| Flammability, UL94 | V-2 @Thickness 0.700 mm | V-2 @Thickness 0.0276 in | |
| V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | ||
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 290 °C | 554 °F | See Materials Notes |
| Mold Temperature | 80.0 °C | 176 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |