- 密度 [g/cm3]: 1.33
- 吸水率 [%]: 0.91
- 缺口冲击强度: 2.0
- 弯曲模量 [MPa]: 6.90
- 热变形温度 [℃]: 261.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | DAM; ASTM D792 | ||
| Density | 1.33 g/cc | 0.0480 lb/in³ | DAM; ISO 1183 | ||
| Filler Content | 33 % | 33 % | DAM | ||
| Water Absorption | 0.91 % @Temperature 23.0 °C | 0.91 % @Temperature 73.4 °F | Immersion 24h; DAM; ISO 62, Similar to | ||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 2.00 mm | 0.0030 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Thickness 2.00 mm | 0.0070 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 112 MPa @Temperature 23.0 °C | 16200 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 148 MPa @Temperature 23.0 °C | 21500 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Tensile Strength | 138 MPa @Temperature 23.0 °C | 20000 psi @Temperature 73.4 °F | DAM; ASTM D638 | ||
| Elongation at Break | 3.2 % @Temperature 23.0 °C | 3.2 % @Temperature 73.4 °F | DAM; ASTM D638 | ||
| 3.6 % @Temperature 23.0 °C | 3.6 % @Temperature 73.4 °F | DAM; ISO 527 | |||
| 6.6 % @Temperature 23.0 °C | 6.6 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 6.50 GPa @Temperature 23.0 °C | 943 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 8.80 GPa @Temperature 23.0 °C | 1280 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Strength | 205 MPa @Temperature 23.0 °C | 29700 psi @Temperature 73.4 °F | DAM; ASTM D790 | ||
| 214 MPa @Temperature 23.0 °C | 31000 psi @Temperature 73.4 °F | DAM; ISO 178 | |||
| Flexural Modulus | 6.90 GPa @Temperature 23.0 °C | 1000 ksi @Temperature 73.4 °F | DAM; ASTM D790 | ||
| 7.60 GPa @Temperature 23.0 °C | 1100 ksi @Temperature 73.4 °F | DAM; ISO 178 | |||
| Izod Impact, Notched | 2.00 J/cm @Temperature 23.0 °C | 3.75 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D256 | ||
| Izod Impact, Unnotched | 13.35 J/cm @Temperature 23.0 °C | 25.01 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D4812 | ||
| Izod Impact, Notched (ISO) | 15.0 kJ/m² @Temperature -40.0 °C | 7.14 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 180/1A | ||
| 16.0 kJ/m² @Temperature -30.0 °C | 7.61 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 180/1A | |||
| 17.0 kJ/m² @Temperature -30.0 °C | 8.09 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 180/1A | |||
| 21.0 kJ/m² @Temperature 23.0 °C | 9.99 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| 26.0 kJ/m² @Temperature 23.0 °C | 12.4 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 87.0 kJ/m² @Temperature -30.0 °C | 41.4 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 180/1U | ||
| Charpy Impact Unnotched | 9.60 J/cm² @Temperature 23.0 °C | 45.7 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eU | ||
| 9.70 J/cm² @Temperature -40.0 °C | 46.2 ft-lb/in² @Temperature -40.0 °F | 50%RH; ISO 179/1eU | |||
| 9.70 J/cm² @Temperature 23.0 °C | 46.2 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| 10.9 J/cm² @Temperature -40.0 °C | 51.9 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.70 J/cm² @Temperature -30.0 °C | 8.09 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eA | ||
| 1.80 J/cm² @Temperature -40.0 °C | 8.57 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 179/1eA | |||
| 1.80 J/cm² @Temperature -30.0 °C | 8.57 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eA | |||
| 2.00 J/cm² @Temperature 23.0 °C | 9.52 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| 2.70 J/cm² @Temperature 23.0 °C | 12.8 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 400 V @Temperature 23.0 °C | 400 V @Temperature 73.4 °F | DAM; UL 746A | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature -40.0 - 23.0 °C | 278 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ASTM E 831 | ||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | |||
| 500 µm/m-°C @Temperature 55.0 - 160 °C | 278 µin/in-°F @Temperature 131 - 320 °F | DAM; ASTM E 831 | |||
| 500 µm/m-°C @Temperature -40.0 - 23.0 °C | 278 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | |||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| 500 µm/m-°C @Temperature 55.0 - 160 °C | 278 µin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 96.0 µm/m-°C @Temperature -40.0 - 23.0 °C | 53.3 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ASTM E 831 | ||
| 96.0 µm/m-°C @Temperature -40.0 - 23.0 °C | 53.3 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | |||
| 119 µm/m-°C @Temperature 23.0 - 55.0 °C | 66.1 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | |||
| 119 µm/m-°C @Temperature 23.0 - 55.0 °C | 66.1 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| 130 µm/m-°C @Temperature 55.0 - 160 °C | 72.2 µin/in-°F @Temperature 131 - 320 °F | DAM; ASTM E 831 | |||
| 130 µm/m-°C @Temperature 55.0 - 160 °C | 72.2 µin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
| Melting Point | 263 °C | 505 °F | DAM; ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 261 °C | 502 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | DAM; ISO 75-1/-2 | ||
| 245 °C | 473 °F | DAM; ASTM D648 | |||
| UL RTI, Electrical | 130 °C @Thickness 0.750 mm | 266 °F @Thickness 0.0295 in | DAM; UL 746B | ||
| 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | DAM; UL 746B | |||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.750 mm | 149 °F @Thickness 0.0295 in | DAM; UL 746B | ||
| 105 °C @Thickness 3.00 mm | 221 °F @Thickness 0.118 in | DAM; UL 746B | |||
| 105 °C @Thickness 1.50 mm | 221 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| UL RTI, Mechanical without Impact | 85.0 °C @Thickness 0.750 mm | 185 °F @Thickness 0.0295 in | DAM; UL 746B | ||
| 95.0 °C @Thickness 1.50 mm | 203 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 105 °C @Thickness 3.00 mm | 221 °F @Thickness 0.118 in | DAM; UL 746B | |||
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | DAM; IEC 60695-11-10 | ||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; UL94 | |||
| HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | DAM; UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 262 °C | 504 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 295 °C | 563 °F | DAM; Optimum | |||
| 285 - 305 °C | 545 - 581 °F | DAM | |||
| Mold Temperature | 50.0 - 100 °C | 122 - 212 °F | DAM | ||
| 80.0 °C | 176 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Additive | Heat Stabilizer | DAM | |||
| Impact Modifier | DAM | ||||
| Appearance | Black Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Features | Heat Resistance, Good | DAM | |||
| Impact Resistance, High | DAM | ||||
| Toughness, Good | DAM | ||||
| Filler | Glass fiber reinforcement | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Heat Stabilized | Yes | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66-IGF33< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA66 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Glass Reinforced Resins | DAM | |||
| Toughened Resins | DAM | ||||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA66-IGF33 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Ultrasonic Weldable | Yes | DAM | |||
| Uses | Appliance Components | DAM | |||
| Automotive Applications | DAM | ||||
| Fasteners | DAM | ||||
| Industrial Applications | DAM | ||||
| Sporting Goods | DAM | ||||