- 密度 [g/cm3]: 1.31
- 缺口冲击强度: 25.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | DAM; ISO 1183 | ||
| Filler Content | 33 % | 33 % | DAM | ||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 2.00 mm | 0.0030 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Thickness 2.00 mm | 0.0080 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 104 MPa @Temperature 23.0 °C | 15100 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 143 MPa @Temperature 23.0 °C | 20700 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 4.5 % @Temperature 23.0 °C | 4.5 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 8.5 % @Temperature 23.0 °C | 8.5 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 6.00 GPa @Temperature 23.0 °C | 870 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 8.90 GPa @Temperature 23.0 °C | 1290 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Izod Impact, Notched (ISO) | 25.0 kJ/m² @Temperature 23.0 °C | 11.9 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | ||
| 27.0 kJ/m² @Temperature 23.0 °C | 12.8 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Charpy Impact Unnotched | 9.80 J/cm² @Temperature 23.0 °C | 46.6 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eU | ||
| 10.3 J/cm² @Temperature 23.0 °C | 49.0 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 2.70 J/cm² @Temperature 23.0 °C | 12.8 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
| 2.80 J/cm² @Temperature 23.0 °C | 13.3 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 262 °C | 504 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 290 °C | 554 °F | DAM; Optimum | |||
| 285 - 305 °C | 545 - 581 °F | DAM | |||
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | DAM | ||
| 70.0 °C | 158 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Appearance | Black Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Filler | Glass Fiber Reinforced | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Material Status | Current | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Glass Reinforced Resins | DAM | |||
| Toughened Resins | DAM | ||||
| RoHS Compliance | Contact Manufacturer | DAM | |||