DuPont Performance Polymers Zytel® 80G43HS1L BK104 Nylon 66

DuPont Performance Polymers Zytel® 80G43HS1L BK104 Nylon 66 物性表: DuPont Performance Polymers Zytel® 80G43HS1L BK104 Nylon 66物性表及特性介绍,DuPont Performance Polymers Zytel® 80G43HS1L BK104 Nylon 66注塑参数详情,如需DuPont Performance Polymers Zytel® 80G43HS1L BK104 Nylon 66下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.43
  • 吸水率 [%]: 1.5
  • 缺口冲击强度: 2.35
  • 弯曲模量 [MPa]: 6.90
  • 热变形温度 [℃]: 261.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.43 g/cc1.43 g/ccDAM; ASTM D792
Density 1.43 g/cc0.0517 lb/in³DAM; ISO 1183
Filler Content 43 %43 %DAM
Water Absorption  1.5 %
@Thickness 1.00 mm,
Temperature 23.0 °C		1.5 %
@Thickness 0.0394 in,
Temperature 73.4 °F		Equilibrium 50%RH; DAM; ISO 62, Similar to
 4.9 %
@Thickness 1.00 mm,
Temperature 23.0 °C		4.9 %
@Thickness 0.0394 in,
Temperature 73.4 °F		Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.0020 cm/cm
@Thickness 2.00 mm		0.0020 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
@Thickness 2.00 mm		0.0060 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 169 MPa
@Temperature 23.0 °C		24500 psi
@Temperature 73.4 °F		DAM; ISO 527
Tensile Strength  117 MPa
@Temperature 23.0 °C		17000 psi
@Temperature 73.4 °F		50%RH; ASTM D638
 152 MPa
@Temperature 23.0 °C		22000 psi
@Temperature 73.4 °F		DAM; ASTM D638
Tensile Stress  5.90 MPa
@Strain 0.100 %,
Temperature 100 °C		856 psi
@Strain 0.100 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 8.66 MPa
@Strain 0.200 %,
Temperature 150 °C		1260 psi
@Strain 0.200 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 11.6 MPa
@Strain 0.200 %,
Temperature 100 °C		1680 psi
@Strain 0.200 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 12.0 MPa
@Strain 0.100 %,
Temperature 23.0 °C		1740 psi
@Strain 0.100 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 12.2 MPa
@Strain 0.100 %,
Temperature -40.0 °C		1770 psi
@Strain 0.100 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 12.44 MPa
@Strain 0.300 %,
Temperature 150 °C		1804 psi
@Strain 0.300 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 15.74 MPa
@Strain 0.400 %,
Temperature 150 °C		2283 psi
@Strain 0.400 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 16.79 MPa
@Strain 0.300 %,
Temperature 100 °C		2435 psi
@Strain 0.300 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 18.66 MPa
@Strain 0.500 %,
Temperature 150 °C		2706 psi
@Strain 0.500 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 21.19 MPa
@Strain 0.400 %,
Temperature 100 °C		3073 psi
@Strain 0.400 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 21.27 MPa
@Strain 0.600 %,
Temperature 150 °C		3085 psi
@Strain 0.600 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 23.76 MPa
@Strain 0.700 %,
Temperature 150 °C		3446 psi
@Strain 0.700 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 25.41 MPa
@Strain 0.500 %,
Temperature 100 °C		3685 psi
@Strain 0.500 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 25.98 MPa
@Strain 0.800 %,
Temperature 150 °C		3768 psi
@Strain 0.800 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 29.36 MPa
@Strain 0.600 %,
Temperature 100 °C		4258 psi
@Strain 0.600 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 30.01 MPa
@Strain 1.00 %,
Temperature 150 °C		4353 psi
@Strain 1.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 32.97 MPa
@Strain 0.700 %,
Temperature 100 °C		4782 psi
@Strain 0.700 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 34.77 MPa
@Strain 1.30 %,
Temperature 150 °C		5043 psi
@Strain 1.30 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 35.9 MPa
@Strain 0.300 %,
Temperature 23.0 °C		5210 psi
@Strain 0.300 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 36.27 MPa
@Strain 0.800 %,
Temperature 100 °C		5261 psi
@Strain 0.800 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 36.6 MPa
@Strain 0.300 %,
Temperature -40.0 °C		5310 psi
@Strain 0.300 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 38.83 MPa
@Strain 1.60 %,
Temperature 150 °C		5632 psi
@Strain 1.60 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 42.21 MPa
@Strain 1.00 %,
Temperature 100 °C		6122 psi
@Strain 1.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 44.96 MPa
@Strain 2.20 %,
Temperature 150 °C		6521 psi
@Strain 2.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 47.37 MPa
@Strain 2.50 %,
Temperature 150 °C		6870 psi
@Strain 2.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 47.56 MPa
@Strain 1.20 %,
Temperature 100 °C		6898 psi
@Strain 1.20 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 52.32 MPa
@Strain 1.40 %,
Temperature 100 °C		7588 psi
@Strain 1.40 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 54.48 MPa
@Strain 1.50 %,
Temperature 100 °C		7902 psi
@Strain 1.50 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 55.09 MPa
@Strain 3.90 %,
Temperature 150 °C		7990 psi
@Strain 3.90 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 56.22 MPa
@Strain 4.20 %,
Temperature 150 °C		8154 psi
@Strain 4.20 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 56.9 MPa
@Strain 4.40 %,
Temperature 150 °C		8250 psi
@Strain 4.40 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 57.2 MPa
@Strain 0.500 %,
Temperature 23.0 °C		8300 psi
@Strain 0.500 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 58.63 MPa
@Strain 5.00 %,
Temperature 150 °C		8504 psi
@Strain 5.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 60.32 MPa
@Strain 1.80 %,
Temperature 100 °C		8749 psi
@Strain 1.80 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 60.75 MPa
@Strain 6.00 %,
Temperature 150 °C		8811 psi
@Strain 6.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 61.41 MPa
@Strain 6.50 %,
Temperature 150 °C		8907 psi
@Strain 6.50 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 61.66 MPa
@Strain 7.00 %,
Temperature 150 °C		8943 psi
@Strain 7.00 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 63.67 MPa
@Strain 2.00 %,
Temperature 100 °C		9235 psi
@Strain 2.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 66.96 MPa
@Strain 0.600 %,
Temperature 23.0 °C		9712 psi
@Strain 0.600 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 68.13 MPa
@Strain 2.30 %,
Temperature 100 °C		9881 psi
@Strain 2.30 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 68.46 MPa
@Strain 0.600 %,
Temperature -40.0 °C		9929 psi
@Strain 0.600 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 75.12 MPa
@Strain 2.90 %,
Temperature 100 °C		10900 psi
@Strain 2.90 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 76.36 MPa
@Strain 0.700 %,
Temperature 23.0 °C		11080 psi
@Strain 0.700 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 78.69 MPa
@Strain 0.700 %,
Temperature -40.0 °C		11410 psi
@Strain 0.700 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 81.73 MPa
@Strain 3.70 %,
Temperature 100 °C		11850 psi
@Strain 3.70 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 85.24 MPa
@Strain 0.800 %,
Temperature 23.0 °C		12360 psi
@Strain 0.800 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 88.05 MPa
@Strain 5.00 %,
Temperature 100 °C		12770 psi
@Strain 5.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 90.31 MPa
@Strain 6.00 %,
Temperature 100 °C		13100 psi
@Strain 6.00 %,
Temperature 212 °F		DAM; ISO 11403-1/-2
 93.42 MPa
@Strain 0.900 %,
Temperature 23.0 °C		13550 psi
@Strain 0.900 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 101.03 MPa
@Strain 1.00 %,
Temperature 23.0 °C		14653 psi
@Strain 1.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 107.51 MPa
@Strain 1.00 %,
Temperature -40.0 °C		15593 psi
@Strain 1.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 108.25 MPa
@Strain 1.10 %,
Temperature 23.0 °C		15700 psi
@Strain 1.10 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 114.9 MPa
@Strain 1.20 %,
Temperature 23.0 °C		16660 psi
@Strain 1.20 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 116.67 MPa
@Strain 1.10 %,
Temperature -40.0 °C		16922 psi
@Strain 1.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 120.96 MPa
@Strain 1.30 %,
Temperature 23.0 °C		17544 psi
@Strain 1.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 125.37 MPa
@Strain 1.20 %,
Temperature -40.0 °C		18183 psi
@Strain 1.20 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 126.56 MPa
@Strain 1.40 %,
Temperature 23.0 °C		18356 psi
@Strain 1.40 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 131.68 MPa
@Strain 1.50 %,
Temperature 23.0 °C		19099 psi
@Strain 1.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 133.5 MPa
@Strain 1.30 %,
Temperature -40.0 °C		19360 psi
@Strain 1.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 140.22 MPa
@Strain 1.70 %,
Temperature 23.0 °C		20337 psi
@Strain 1.70 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 143.88 MPa
@Strain 1.80 %,
Temperature 23.0 °C		20868 psi
@Strain 1.80 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 149.21 MPa
@Strain 1.50 %,
Temperature -40.0 °C		21641 psi
@Strain 1.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 150.21 MPa
@Strain 2.00 %,
Temperature 23.0 °C		21786 psi
@Strain 2.00 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 156.6 MPa
@Strain 1.60 %,
Temperature -40.0 °C		22710 psi
@Strain 1.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 160.82 MPa
@Strain 2.50 %,
Temperature 23.0 °C		23325 psi
@Strain 2.50 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 163.31 MPa
@Strain 1.70 %,
Temperature -40.0 °C		23686 psi
@Strain 1.70 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 167.3 MPa
@Strain 3.30 %,
Temperature 23.0 °C		24260 psi
@Strain 3.30 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 182.22 MPa
@Strain 2.00 %,
Temperature -40.0 °C		26429 psi
@Strain 2.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 187.73 MPa
@Strain 2.10 %,
Temperature -40.0 °C		27228 psi
@Strain 2.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 197.77 MPa
@Strain 2.30 %,
Temperature -40.0 °C		28684 psi
@Strain 2.30 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 206.92 MPa
@Strain 2.50 %,
Temperature -40.0 °C		30011 psi
@Strain 2.50 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 211.02 MPa
@Strain 2.60 %,
Temperature -40.0 °C		30606 psi
@Strain 2.60 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 218.56 MPa
@Strain 2.80 %,
Temperature -40.0 °C		31700 psi
@Strain 2.80 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 225.07 MPa
@Strain 3.00 %,
Temperature -40.0 °C		32644 psi
@Strain 3.00 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 227.4 MPa
@Strain 3.10 %,
Temperature -40.0 °C		32980 psi
@Strain 3.10 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
Elongation at Break  3.0 %
@Temperature 23.0 °C		3.0 %
@Temperature 73.4 °F		DAM; ASTM D638
 3.3 %
@Temperature 23.0 °C		3.3 %
@Temperature 73.4 °F		DAM; ISO 527
 4.0 %
@Temperature 23.0 °C		4.0 %
@Temperature 73.4 °F		50%RH; ASTM D638
Tensile Modulus 11.7 GPa
@Temperature 23.0 °C		1700 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Strength 228 MPa
@Temperature 23.0 °C		33100 psi
@Temperature 73.4 °F		DAM; ASTM D790
Flexural Modulus  6.90 GPa
@Temperature 23.0 °C		1000 ksi
@Temperature 73.4 °F		50%RH; ASTM D790
 9.65 GPa
@Temperature 23.0 °C		1400 ksi
@Temperature 73.4 °F		DAM; ASTM D790
 10.3 GPa
@Temperature 23.0 °C		1490 ksi
@Temperature 73.4 °F		DAM; ISO 178
Izod Impact, Notched  2.35 J/cm
@Temperature 23.0 °C		4.40 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D256
 2.65 J/cm
@Temperature 23.0 °C		4.96 ft-lb/in
@Temperature 73.4 °F		50%RH; ASTM D256
Izod Impact, Unnotched 10.7 J/cm
@Temperature 23.0 °C		20.0 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D4812
Izod Impact, Notched (ISO)  14.0 kJ/m²
@Temperature -40.0 °C		6.66 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 180/1A
 23.0 kJ/m²
@Temperature 23.0 °C		10.9 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
Izod Impact, Unnotched (ISO) 78.0 kJ/m²
@Temperature 23.0 °C		37.1 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1U
Charpy Impact Unnotched 9.00 J/cm²
@Temperature 23.0 °C		42.8 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eU
Charpy Impact, Notched  1.50 J/cm²
@Temperature -40.0 °C		7.14 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 179/1eA
 2.30 J/cm²
@Temperature 23.0 °C		10.9 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 
Thermal PropertiesMetricEnglishComments
Melting Point 260 °C500 °FDAM; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 261 °C502 °FDAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 248 °C478 °FDAM; ASTM D648
 250 °C482 °FDAM; ISO 75-1/-2
Flammability, UL94  HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		DAM; IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; UL94
 HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		DAM; UL94
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; UL94
Oxygen Index 27 %27 %DAM; ISO 4589-1/-2
 
Processing PropertiesMetricEnglishComments
Melt Temperature 262 °C504 °F10°C/min; DAM; ISO 11357-1/-3
 295 °C563 °FDAM; Optimum
 285 - 305 °C545 - 581 °FDAM
Mold Temperature 50.0 - 100 °C122 - 212 °FDAM
 80.0 °C176 °FDAM; optimum
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.20 %<= 0.20 %DAM
 
Descriptive Properties
AdditiveHeat StabilizerDAM
 Impact ModifierDAM
AppearanceBlack ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FeaturesHeat StabilizedDAM
 Impact Resistance, HighDAM
 Toughness, GoodDAM
FillerGlass fiber reinforcementDAM
FormsPelletsDAM
GenericNylon 66DAM
Material StatusCurrentDAM
Part Marking Code>PA66-IGF43<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA66DAM
Processing MethodInjection MoldingDAM
Product CategoryGlass Reinforced ResinsDAM
 Toughened ResinsDAM
Region Available - GlobalYesDAM
Resin IdentificationPA66-IGF43ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
UsesAppliance ComponentsDAM
 Automotive ApplicationsDAM
 FastenersDAM
 Industrial ApplicationsDAM
 Sporting GoodsDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45496.html

免责声明: 本文 DuPont Performance Polymers Zytel® 80G43HS1L BK104 Nylon 66 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4