- 密度 [g/cm3]: 1.36
- 吸水率 [%]: 1.9
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | DAM; ISO 1183 | ||
| Filler Content | 30 % | 30 % | DAM | ||
| Water Absorption | 1.9 % @Temperature 23.0 °C | 1.9 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | ||
| 6.0 % @Temperature 23.0 °C | 6.0 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 2.00 mm | 0.0020 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Thickness 2.00 mm | 0.0090 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 137 MPa @Temperature 23.0 °C | 19900 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 193 MPa @Temperature 23.0 °C | 28000 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Tensile Stress | 0.640 MPa @Strain 0.000 %, Temperature 200 °C | 92.8 psi @Strain 0.000 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | ||
| 0.760 MPa @Strain 0.000 %, Temperature 220 °C | 110 psi @Strain 0.000 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 0.810 MPa @Strain 0.000 %, Temperature 150 °C | 117 psi @Strain 0.000 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 0.820 MPa @Strain 0.000 %, Temperature 180 °C | 119 psi @Strain 0.000 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 0.910 MPa @Strain 0.000 %, Temperature 150 °C | 132 psi @Strain 0.000 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 0.940 MPa @Strain 0.000 %, Temperature 120 °C | 136 psi @Strain 0.000 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 1.02 MPa @Strain 0.000 %, Temperature 120 °C | 148 psi @Strain 0.000 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 1.12 MPa @Strain 0.000 %, Temperature 90.0 °C | 162 psi @Strain 0.000 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 1.13 MPa @Strain 0.000 %, Temperature 90.0 °C | 164 psi @Strain 0.000 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 1.17 MPa @Strain 0.000 %, Temperature 60.0 °C | 170 psi @Strain 0.000 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 1.17 MPa @Strain 0.000 %, Temperature 40.0 °C | 170 psi @Strain 0.000 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 1.35 MPa @Strain 0.000 %, Temperature 23.0 °C | 196 psi @Strain 0.000 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 1.45 MPa @Strain 0.000 %, Temperature 0.000 °C | 210 psi @Strain 0.000 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 1.46 MPa @Strain 0.000 %, Temperature 60.0 °C | 212 psi @Strain 0.000 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 1.66 MPa @Strain 0.000 %, Temperature 0.000 °C | 241 psi @Strain 0.000 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 1.77 MPa @Strain 0.000 %, Temperature 23.0 °C | 257 psi @Strain 0.000 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 1.82 MPa @Strain 0.000 %, Temperature 40.0 °C | 264 psi @Strain 0.000 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 1.86 MPa @Strain 0.000 %, Temperature -20.0 °C | 270 psi @Strain 0.000 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 1.88 MPa @Strain 0.000 %, Temperature -20.0 °C | 273 psi @Strain 0.000 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 2.50 MPa @Strain 0.0500 %, Temperature -20.0 °C | 363 psi @Strain 0.0500 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 2.64 MPa @Strain 0.0500 %, Temperature -20.0 °C | 383 psi @Strain 0.0500 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 2.93 MPa @Strain 0.0500 %, Temperature 0.000 °C | 425 psi @Strain 0.0500 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 3.66 MPa @Strain 0.0800 %, Temperature 220 °C | 531 psi @Strain 0.0800 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 3.69 MPa @Strain 0.0800 %, Temperature 150 °C | 535 psi @Strain 0.0800 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 3.74 MPa @Strain 0.0800 %, Temperature 120 °C | 542 psi @Strain 0.0800 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 3.76 MPa @Strain 0.100 %, Temperature 200 °C | 545 psi @Strain 0.100 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 4.01 MPa @Strain 0.0900 %, Temperature 180 °C | 582 psi @Strain 0.0900 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 4.17 MPa @Strain 0.0800 %, Temperature 150 °C | 605 psi @Strain 0.0800 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 4.17 MPa @Strain 0.0700 %, Temperature 90.0 °C | 605 psi @Strain 0.0700 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 4.27 MPa @Strain 0.0700 %, Temperature 120 °C | 619 psi @Strain 0.0700 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 4.45 MPa @Strain 0.0700 %, Temperature 60.0 °C | 645 psi @Strain 0.0700 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 4.67 MPa @Strain 0.0600 %, Temperature 40.0 °C | 677 psi @Strain 0.0600 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 4.71 MPa @Strain 0.0800 %, Temperature 90.0 °C | 683 psi @Strain 0.0800 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 4.97 MPa @Strain 0.0500 %, Temperature 23.0 °C | 721 psi @Strain 0.0500 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 5.14 MPa @Strain 0.0600 %, Temperature 60.0 °C | 745 psi @Strain 0.0600 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 5.52 MPa @Strain 0.0400 %, Temperature 0.000 °C | 801 psi @Strain 0.0400 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 5.71 MPa @Strain 0.0400 %, Temperature 23.0 °C | 828 psi @Strain 0.0400 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 5.72 MPa @Strain 0.0400 %, Temperature 40.0 °C | 830 psi @Strain 0.0400 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 6.34 MPa @Strain 0.180 %, Temperature 220 °C | 920 psi @Strain 0.180 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 6.39 MPa @Strain 0.140 %, Temperature 120 °C | 927 psi @Strain 0.140 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 6.44 MPa @Strain 0.160 %, Temperature 150 °C | 934 psi @Strain 0.160 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 6.68 MPa @Strain 0.210 %, Temperature 200 °C | 969 psi @Strain 0.210 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 7.11 MPa @Strain 0.180 %, Temperature 180 °C | 1030 psi @Strain 0.180 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 7.21 MPa @Strain 0.100 %, Temperature -20.0 °C | 1050 psi @Strain 0.100 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 7.22 MPa @Strain 0.140 %, Temperature 90.0 °C | 1050 psi @Strain 0.140 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 7.40 MPa @Strain 0.160 %, Temperature 150 °C | 1070 psi @Strain 0.160 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 7.51 MPa @Strain 0.150 %, Temperature 120 °C | 1090 psi @Strain 0.150 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 7.57 MPa @Strain 0.100 %, Temperature 0.000 °C | 1100 psi @Strain 0.100 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 7.73 MPa @Strain 0.0900 %, Temperature -20.0 °C | 1120 psi @Strain 0.0900 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 7.81 MPa @Strain 0.130 %, Temperature 60.0 °C | 1130 psi @Strain 0.130 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 8.12 MPa @Strain 0.110 %, Temperature 40.0 °C | 1180 psi @Strain 0.110 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 8.26 MPa @Strain 0.150 %, Temperature 90.0 °C | 1200 psi @Strain 0.150 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 8.71 MPa @Strain 0.100 %, Temperature 23.0 °C | 1260 psi @Strain 0.100 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 8.84 MPa @Strain 0.110 %, Temperature 60.0 °C | 1280 psi @Strain 0.110 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 8.94 MPa @Strain 0.200 %, Temperature 120 °C | 1300 psi @Strain 0.200 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 9.05 MPa @Strain 0.240 %, Temperature 150 °C | 1310 psi @Strain 0.240 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 9.68 MPa @Strain 0.0900 %, Temperature 0.000 °C | 1400 psi @Strain 0.0900 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 9.80 MPa @Strain 0.0800 %, Temperature 23.0 °C | 1420 psi @Strain 0.0800 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 9.88 MPa @Strain 0.0900 %, Temperature 40.0 °C | 1430 psi @Strain 0.0900 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 10.02 MPa @Strain 0.200 %, Temperature 90.0 °C | 1453 psi @Strain 0.200 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 10.48 MPa @Strain 0.270 %, Temperature 180 °C | 1520 psi @Strain 0.270 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 10.56 MPa @Strain 0.240 %, Temperature 150 °C | 1532 psi @Strain 0.240 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 10.6 MPa @Strain 0.220 %, Temperature 120 °C | 1540 psi @Strain 0.220 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 10.94 MPa @Strain 0.180 %, Temperature 60.0 °C | 1587 psi @Strain 0.180 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 11.26 MPa @Strain 0.360 %, Temperature 220 °C | 1633 psi @Strain 0.360 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 11.44 MPa @Strain 0.170 %, Temperature 40.0 °C | 1659 psi @Strain 0.170 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 11.62 MPa @Strain 0.210 %, Temperature 90.0 °C | 1685 psi @Strain 0.210 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 11.96 MPa @Strain 0.130 %, Temperature -20.0 °C | 1735 psi @Strain 0.130 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 12.19 MPa @Strain 0.140 %, Temperature 0.000 °C | 1768 psi @Strain 0.140 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 12.31 MPa @Strain 0.160 %, Temperature 23.0 °C | 1785 psi @Strain 0.160 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 12.52 MPa @Strain 0.160 %, Temperature 60.0 °C | 1816 psi @Strain 0.160 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 12.53 MPa @Strain 0.150 %, Temperature -20.0 °C | 1817 psi @Strain 0.150 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 13.72 MPa @Strain 0.130 %, Temperature 0.000 °C | 1990 psi @Strain 0.130 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 13.92 MPa @Strain 0.440 %, Temperature 200 °C | 2019 psi @Strain 0.440 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 13.97 MPa @Strain 0.130 %, Temperature 23.0 °C | 2026 psi @Strain 0.130 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 14.01 MPa @Strain 0.140 %, Temperature 40.0 °C | 2032 psi @Strain 0.140 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 14.01 MPa @Strain 0.240 %, Temperature 60.0 °C | 2032 psi @Strain 0.240 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 14.03 MPa @Strain 0.290 %, Temperature 90.0 °C | 2035 psi @Strain 0.290 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 14.52 MPa @Strain 0.230 %, Temperature 40.0 °C | 2106 psi @Strain 0.230 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 14.59 MPa @Strain 0.350 %, Temperature 120 °C | 2116 psi @Strain 0.350 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 15.91 MPa @Strain 0.210 %, Temperature 23.0 °C | 2308 psi @Strain 0.210 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 16.06 MPa @Strain 0.210 %, Temperature 60.0 °C | 2329 psi @Strain 0.210 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 16.68 MPa @Strain 0.180 %, Temperature -20.0 °C | 2419 psi @Strain 0.180 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 16.8 MPa @Strain 0.190 %, Temperature 0.000 °C | 2440 psi @Strain 0.190 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 17.39 MPa @Strain 0.190 %, Temperature -20.0 °C | 2522 psi @Strain 0.190 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 17.79 MPa @Strain 0.180 %, Temperature 0.000 °C | 2580 psi @Strain 0.180 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 17.98 MPa @Strain 0.170 %, Temperature 40.0 °C | 2608 psi @Strain 0.170 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 18.03 MPa @Strain 0.170 %, Temperature 23.0 °C | 2615 psi @Strain 0.170 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 18.68 MPa @Strain 0.550 %, Temperature 150 °C | 2709 psi @Strain 0.550 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 20.83 MPa @Strain 0.400 %, Temperature 90.0 °C | 3021 psi @Strain 0.400 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 20.96 MPa @Strain 0.830 %, Temperature 220 °C | 3040 psi @Strain 0.830 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 21.04 MPa @Strain 0.220 %, Temperature -20.0 °C | 3052 psi @Strain 0.220 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 21.13 MPa @Strain 0.240 %, Temperature 0.000 °C | 3065 psi @Strain 0.240 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 21.4 MPa @Strain 0.470 %, Temperature 120 °C | 3100 psi @Strain 0.470 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 21.75 MPa @Strain 0.290 %, Temperature 60.0 °C | 3155 psi @Strain 0.290 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 21.75 MPa @Strain 0.220 %, Temperature 0.000 °C | 3155 psi @Strain 0.220 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 21.85 MPa @Strain 0.220 %, Temperature 40.0 °C | 3169 psi @Strain 0.220 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 21.97 MPa @Strain 0.240 %, Temperature -20.0 °C | 3186 psi @Strain 0.240 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 22.26 MPa @Strain 0.210 %, Temperature 23.0 °C | 3229 psi @Strain 0.210 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 23.35 MPa @Strain 0.710 %, Temperature 180 °C | 3387 psi @Strain 0.710 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 23.57 MPa @Strain 0.330 %, Temperature 23.0 °C | 3419 psi @Strain 0.330 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 23.66 MPa @Strain 0.610 %, Temperature 150 °C | 3432 psi @Strain 0.610 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 24.25 MPa @Strain 0.940 %, Temperature 200 °C | 3517 psi @Strain 0.940 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 25.21 MPa @Strain 0.420 %, Temperature 40.0 °C | 3656 psi @Strain 0.420 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 25.3 MPa @Strain 0.690 %, Temperature 120 °C | 3670 psi @Strain 0.690 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 26.39 MPa @Strain 0.600 %, Temperature 90.0 °C | 3828 psi @Strain 0.600 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 26.43 MPa @Strain 0.490 %, Temperature 60.0 °C | 3833 psi @Strain 0.490 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 27.11 MPa @Strain 0.270 %, Temperature 23.0 °C | 3932 psi @Strain 0.270 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 27.47 MPa @Strain 1.33 %, Temperature 220 °C | 3984 psi @Strain 1.33 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 27.92 MPa @Strain 0.940 %, Temperature 150 °C | 4049 psi @Strain 0.940 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 28.63 MPa @Strain 0.290 %, Temperature 40.0 °C | 4152 psi @Strain 0.290 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 29.69 MPa @Strain 0.290 %, Temperature -20.0 °C | 4306 psi @Strain 0.290 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 29.87 MPa @Strain 0.310 %, Temperature 0.000 °C | 4332 psi @Strain 0.310 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 31.89 MPa @Strain 1.46 %, Temperature 200 °C | 4625 psi @Strain 1.46 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 32.64 MPa @Strain 1.84 %, Temperature 220 °C | 4734 psi @Strain 1.84 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 32.88 MPa @Strain 1.15 %, Temperature 180 °C | 4769 psi @Strain 1.15 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 33.24 MPa @Strain 0.820 %, Temperature 120 °C | 4821 psi @Strain 0.820 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 33.85 MPa @Strain 1.02 %, Temperature 120 °C | 4910 psi @Strain 1.02 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 34.1 MPa @Strain 1.00 %, Temperature 150 °C | 4950 psi @Strain 1.00 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 34.24 MPa @Strain 0.700 %, Temperature 90.0 °C | 4966 psi @Strain 0.700 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 35.03 MPa @Strain 1.32 %, Temperature 150 °C | 5081 psi @Strain 1.32 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 35.61 MPa @Strain 0.890 %, Temperature 90.0 °C | 5165 psi @Strain 0.890 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 35.87 MPa @Strain 0.380 %, Temperature 0.000 °C | 5203 psi @Strain 0.380 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 35.92 MPa @Strain 0.640 %, Temperature 40.0 °C | 5210 psi @Strain 0.640 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 36.56 MPa @Strain 0.530 %, Temperature 23.0 °C | 5303 psi @Strain 0.530 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 36.7 MPa @Strain 2.34 %, Temperature 220 °C | 5320 psi @Strain 2.34 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 36.92 MPa @Strain 0.750 %, Temperature 60.0 °C | 5355 psi @Strain 0.750 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 37.6 MPa @Strain 1.96 %, Temperature 200 °C | 5450 psi @Strain 1.96 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 39.01 MPa @Strain 0.520 %, Temperature 60.0 °C | 5658 psi @Strain 0.520 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 39.58 MPa @Strain 0.410 %, Temperature -20.0 °C | 5741 psi @Strain 0.410 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 40.12 MPa @Strain 2.83 %, Temperature 220 °C | 5819 psi @Strain 2.83 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 40.41 MPa @Strain 1.61 %, Temperature 180 °C | 5861 psi @Strain 1.61 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 40.54 MPa @Strain 1.31 %, Temperature 120 °C | 5880 psi @Strain 1.31 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 40.97 MPa @Strain 1.69 %, Temperature 150 °C | 5942 psi @Strain 1.69 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 42.11 MPa @Strain 1.36 %, Temperature 150 °C | 6108 psi @Strain 1.36 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 42.11 MPa @Strain 1.13 %, Temperature 120 °C | 6108 psi @Strain 1.13 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 42.38 MPa @Strain 2.44 %, Temperature 200 °C | 6147 psi @Strain 2.44 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 43.14 MPa @Strain 3.35 %, Temperature 220 °C | 6257 psi @Strain 3.35 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 43.31 MPa @Strain 1.17 %, Temperature 90.0 °C | 6282 psi @Strain 1.17 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 43.58 MPa @Strain 0.460 %, Temperature 40.0 °C | 6321 psi @Strain 0.460 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 43.7 MPa @Strain 0.830 %, Temperature 40.0 °C | 6340 psi @Strain 0.830 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 43.8 MPa @Strain 0.970 %, Temperature 90.0 °C | 6350 psi @Strain 0.970 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 44.19 MPa @Strain 0.960 %, Temperature 60.0 °C | 6409 psi @Strain 0.960 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 45.36 MPa @Strain 0.690 %, Temperature 23.0 °C | 6579 psi @Strain 0.690 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 45.76 MPa @Strain 3.85 %, Temperature 220 °C | 6637 psi @Strain 3.85 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 46.24 MPa @Strain 2.05 %, Temperature 180 °C | 6707 psi @Strain 2.05 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 46.27 MPa @Strain 2.08 %, Temperature 150 °C | 6711 psi @Strain 2.08 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 46.49 MPa @Strain 2.94 %, Temperature 200 °C | 6743 psi @Strain 2.94 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 46.66 MPa @Strain 1.62 %, Temperature 120 °C | 6767 psi @Strain 1.62 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 47.63 MPa @Strain 0.470 %, Temperature 23.0 °C | 6908 psi @Strain 0.470 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 48.09 MPa @Strain 4.36 %, Temperature 220 °C | 6975 psi @Strain 4.36 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 49.19 MPa @Strain 1.73 %, Temperature 150 °C | 7134 psi @Strain 1.73 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 49.35 MPa @Strain 0.510 %, Temperature 0.000 °C | 7158 psi @Strain 0.510 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 50.12 MPa @Strain 3.45 %, Temperature 200 °C | 7269 psi @Strain 3.45 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 50.16 MPa @Strain 4.83 %, Temperature 220 °C | 7275 psi @Strain 4.83 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 50.18 MPa @Strain 1.45 %, Temperature 120 °C | 7278 psi @Strain 1.45 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 50.36 MPa @Strain 1.45 %, Temperature 90.0 °C | 7304 psi @Strain 1.45 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 50.69 MPa @Strain 2.47 %, Temperature 150 °C | 7352 psi @Strain 2.47 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 50.79 MPa @Strain 0.490 %, Temperature -20.0 °C | 7366 psi @Strain 0.490 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 51.12 MPa @Strain 1.17 %, Temperature 60.0 °C | 7414 psi @Strain 1.17 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 51.16 MPa @Strain 2.48 %, Temperature 180 °C | 7420 psi @Strain 2.48 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 51.17 MPa @Strain 0.720 %, Temperature 60.0 °C | 7422 psi @Strain 0.720 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 51.51 MPa @Strain 1.03 %, Temperature 40.0 °C | 7471 psi @Strain 1.03 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 51.85 MPa @Strain 1.22 %, Temperature 90.0 °C | 7520 psi @Strain 1.22 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 52.04 MPa @Strain 5.36 %, Temperature 220 °C | 7548 psi @Strain 5.36 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 52.26 MPa @Strain 1.95 %, Temperature 120 °C | 7580 psi @Strain 1.95 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 53.3 MPa @Strain 0.560 %, Temperature 0.000 °C | 7730 psi @Strain 0.560 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 53.33 MPa @Strain 3.97 %, Temperature 200 °C | 7735 psi @Strain 3.97 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 53.72 MPa @Strain 5.90 %, Temperature 220 °C | 7791 psi @Strain 5.90 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 53.73 MPa @Strain 0.870 %, Temperature 23.0 °C | 7793 psi @Strain 0.870 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 54.55 MPa @Strain 2.87 %, Temperature 150 °C | 7912 psi @Strain 2.87 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 55.34 MPa @Strain 6.48 %, Temperature 220 °C | 8026 psi @Strain 6.48 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 55.36 MPa @Strain 2.92 %, Temperature 180 °C | 8029 psi @Strain 2.92 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 55.53 MPa @Strain 2.12 %, Temperature 150 °C | 8054 psi @Strain 2.12 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 56.12 MPa @Strain 4.46 %, Temperature 200 °C | 8140 psi @Strain 4.46 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 56.53 MPa @Strain 0.600 %, Temperature 40.0 °C | 8199 psi @Strain 0.600 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 56.81 MPa @Strain 7.01 %, Temperature 220 °C | 8240 psi @Strain 7.01 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 56.85 MPa @Strain 1.74 %, Temperature 90.0 °C | 8245 psi @Strain 1.74 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 57.06 MPa @Strain 1.76 %, Temperature 120 °C | 8276 psi @Strain 1.76 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 57.15 MPa @Strain 2.28 %, Temperature 120 °C | 8289 psi @Strain 2.28 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 57.89 MPa @Strain 1.39 %, Temperature 60.0 °C | 8396 psi @Strain 1.39 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 57.97 MPa @Strain 3.30 %, Temperature 150 °C | 8408 psi @Strain 3.30 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 58.21 MPa @Strain 7.58 %, Temperature 220 °C | 8443 psi @Strain 7.58 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 58.64 MPa @Strain 4.99 %, Temperature 200 °C | 8505 psi @Strain 4.99 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 58.99 MPa @Strain 1.24 %, Temperature 40.0 °C | 8556 psi @Strain 1.24 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 59.12 MPa @Strain 3.38 %, Temperature 180 °C | 8575 psi @Strain 3.38 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 59.46 MPa @Strain 8.14 %, Temperature 220 °C | 8624 psi @Strain 8.14 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 59.53 MPa @Strain 1.49 %, Temperature 90.0 °C | 8634 psi @Strain 1.49 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 60.53 MPa @Strain 8.76 %, Temperature 220 °C | 8779 psi @Strain 8.76 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 60.75 MPa @Strain 2.50 %, Temperature 150 °C | 8811 psi @Strain 2.50 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 60.91 MPa @Strain 5.57 %, Temperature 200 °C | 8834 psi @Strain 5.57 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 60.91 MPa @Strain 0.620 %, Temperature -20.0 °C | 8834 psi @Strain 0.620 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 60.92 MPa @Strain 3.77 %, Temperature 150 °C | 8836 psi @Strain 3.77 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 61.41 MPa @Strain 2.61 %, Temperature 120 °C | 8907 psi @Strain 2.61 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 61.51 MPa @Strain 9.35 %, Temperature 220 °C | 8921 psi @Strain 9.35 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 61.87 MPa @Strain 1.05 %, Temperature 23.0 °C | 8974 psi @Strain 1.05 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 62.39 MPa @Strain 9.94 %, Temperature 220 °C | 9049 psi @Strain 9.94 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 62.39 MPa @Strain 0.910 %, Temperature 60.0 °C | 9049 psi @Strain 0.910 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 62.41 MPa @Strain 3.85 %, Temperature 180 °C | 9052 psi @Strain 3.85 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 62.48 MPa @Strain 2.03 %, Temperature 90.0 °C | 9062 psi @Strain 2.03 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 62.73 MPa @Strain 0.670 %, Temperature 0.000 °C | 9098 psi @Strain 0.670 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 62.96 MPa @Strain 6.16 %, Temperature 200 °C | 9132 psi @Strain 6.16 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 63.22 MPa @Strain 10.52 %, Temperature 220 °C | 9169 psi @Strain 10.52 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 63.38 MPa @Strain 2.09 %, Temperature 120 °C | 9193 psi @Strain 2.09 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 63.45 MPa @Strain 4.20 %, Temperature 150 °C | 9203 psi @Strain 4.20 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 63.82 MPa @Strain 11.13 %, Temperature 220 °C | 9256 psi @Strain 11.13 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 63.91 MPa @Strain 11.82 %, Temperature 220 °C | 9269 psi @Strain 11.82 %, Temperature 428 °F | DAM; ISO 11403-1/-2 | |||
| 64.07 MPa @Strain 0.650 %, Temperature 23.0 °C | 9293 psi @Strain 0.650 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 64.42 MPa @Strain 1.63 %, Temperature 60.0 °C | 9343 psi @Strain 1.63 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 64.81 MPa @Strain 6.71 %, Temperature 200 °C | 9400 psi @Strain 6.71 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 65.17 MPa @Strain 0.620 %, Temperature -20.0 °C | 9452 psi @Strain 0.620 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 65.19 MPa @Strain 2.98 %, Temperature 120 °C | 9455 psi @Strain 2.98 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 65.37 MPa @Strain 4.31 %, Temperature 180 °C | 9481 psi @Strain 4.31 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 65.5 MPa @Strain 2.89 %, Temperature 150 °C | 9500 psi @Strain 2.89 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 65.62 MPa @Strain 4.74 %, Temperature 150 °C | 9517 psi @Strain 4.74 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 66.37 MPa @Strain 7.27 %, Temperature 200 °C | 9626 psi @Strain 7.27 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 66.38 MPa @Strain 1.46 %, Temperature 40.0 °C | 9628 psi @Strain 1.46 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 66.76 MPa @Strain 1.76 %, Temperature 90.0 °C | 9683 psi @Strain 1.76 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 67.4 MPa @Strain 5.28 %, Temperature 150 °C | 9780 psi @Strain 5.28 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 67.42 MPa @Strain 2.33 %, Temperature 90.0 °C | 9778 psi @Strain 2.33 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 67.59 MPa @Strain 0.730 %, Temperature 40.0 °C | 9803 psi @Strain 0.730 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 67.83 MPa @Strain 7.87 %, Temperature 200 °C | 9838 psi @Strain 7.87 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 67.89 MPa @Strain 0.710 %, Temperature 0.000 °C | 9847 psi @Strain 0.710 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 67.92 MPa @Strain 4.79 %, Temperature 180 °C | 9851 psi @Strain 4.79 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 68.41 MPa @Strain 3.36 %, Temperature 120 °C | 9922 psi @Strain 3.36 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 68.87 MPa @Strain 5.82 %, Temperature 150 °C | 9989 psi @Strain 5.82 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 69.16 MPa @Strain 8.51 %, Temperature 200 °C | 10030 psi @Strain 8.51 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 69.27 MPa @Strain 2.42 %, Temperature 120 °C | 10050 psi @Strain 2.42 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 69.65 MPa @Strain 3.29 %, Temperature 150 °C | 10100 psi @Strain 3.29 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 70.1 MPa @Strain 6.39 %, Temperature 150 °C | 10200 psi @Strain 6.39 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 70.15 MPa @Strain 1.25 %, Temperature 23.0 °C | 10170 psi @Strain 1.25 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 70.23 MPa @Strain 5.35 %, Temperature 180 °C | 10190 psi @Strain 5.35 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 70.3 MPa @Strain 9.15 %, Temperature 200 °C | 10200 psi @Strain 9.15 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 70.71 MPa @Strain 1.89 %, Temperature 60.0 °C | 10260 psi @Strain 1.89 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 71.08 MPa @Strain 6.96 %, Temperature 150 °C | 10310 psi @Strain 6.96 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 71.25 MPa @Strain 3.78 %, Temperature 120 °C | 10330 psi @Strain 3.78 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 71.32 MPa @Strain 9.79 %, Temperature 200 °C | 10340 psi @Strain 9.79 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 71.62 MPa @Strain 11.02 %, Temperature 150 °C | 10390 psi @Strain 11.02 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 71.86 MPa @Strain 1.10 %, Temperature 60.0 °C | 10420 psi @Strain 1.10 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 71.89 MPa @Strain 7.55 %, Temperature 150 °C | 10430 psi @Strain 7.55 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 72.11 MPa @Strain 2.66 %, Temperature 90.0 °C | 10460 psi @Strain 2.66 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 72.12 MPa @Strain 10.41 %, Temperature 200 °C | 10460 psi @Strain 10.41 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 72.25 MPa @Strain 5.92 %, Temperature 180 °C | 10480 psi @Strain 5.92 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 72.44 MPa @Strain 8.18 %, Temperature 150 °C | 10510 psi @Strain 8.18 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 72.78 MPa @Strain 11.07 %, Temperature 200 °C | 10560 psi @Strain 11.07 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 72.85 MPa @Strain 8.86 %, Temperature 150 °C | 10570 psi @Strain 8.86 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 72.94 MPa @Strain 12.47 %, Temperature 200 °C | 10580 psi @Strain 12.47 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 72.99 MPa @Strain 10.21 %, Temperature 150 °C | 10590 psi @Strain 10.21 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 73.06 MPa @Strain 9.53 %, Temperature 150 °C | 10600 psi @Strain 9.53 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 73.23 MPa @Strain 0.800 %, Temperature 0.000 °C | 10620 psi @Strain 0.800 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 73.27 MPa @Strain 11.77 %, Temperature 200 °C | 10630 psi @Strain 11.77 %, Temperature 392 °F | DAM; ISO 11403-1/-2 | |||
| 73.44 MPa @Strain 3.73 %, Temperature 150 °C | 10650 psi @Strain 3.73 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 73.56 MPa @Strain 4.17 %, Temperature 120 °C | 10670 psi @Strain 4.17 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 73.57 MPa @Strain 1.70 %, Temperature 40.0 °C | 10670 psi @Strain 1.70 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 73.76 MPa @Strain 2.05 %, Temperature 90.0 °C | 10700 psi @Strain 2.05 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 74.06 MPa @Strain 6.47 %, Temperature 180 °C | 10740 psi @Strain 6.47 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 74.39 MPa @Strain 0.760 %, Temperature -20.0 °C | 10790 psi @Strain 0.760 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 74.65 MPa @Strain 2.78 %, Temperature 120 °C | 10830 psi @Strain 2.78 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 75.48 MPa @Strain 4.63 %, Temperature 120 °C | 10950 psi @Strain 4.63 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 75.63 MPa @Strain 7.03 %, Temperature 180 °C | 10970 psi @Strain 7.03 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 76.12 MPa @Strain 3.02 %, Temperature 90.0 °C | 11040 psi @Strain 3.02 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 76.69 MPa @Strain 4.14 %, Temperature 150 °C | 11120 psi @Strain 4.14 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 76.71 MPa @Strain 2.17 %, Temperature 60.0 °C | 11130 psi @Strain 2.17 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 77.06 MPa @Strain 7.61 %, Temperature 180 °C | 11180 psi @Strain 7.61 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 77.07 MPa @Strain 5.15 %, Temperature 120 °C | 11180 psi @Strain 5.15 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 77.38 MPa @Strain 0.740 %, Temperature -20.0 °C | 11220 psi @Strain 0.740 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 77.71 MPa @Strain 0.790 %, Temperature 23.0 °C | 11270 psi @Strain 0.790 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 78.0 MPa @Strain 1.46 %, Temperature 23.0 °C | 11300 psi @Strain 1.46 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 78.07 MPa @Strain 0.860 %, Temperature 40.0 °C | 11320 psi @Strain 0.860 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 78.28 MPa @Strain 8.24 %, Temperature 180 °C | 11350 psi @Strain 8.24 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 78.33 MPa @Strain 5.68 %, Temperature 120 °C | 11360 psi @Strain 5.68 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 79.29 MPa @Strain 8.87 %, Temperature 180 °C | 11500 psi @Strain 8.87 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 79.33 MPa @Strain 6.21 %, Temperature 120 °C | 11510 psi @Strain 6.21 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 79.45 MPa @Strain 3.39 %, Temperature 90.0 °C | 11520 psi @Strain 3.39 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 79.48 MPa @Strain 4.62 %, Temperature 150 °C | 11530 psi @Strain 4.62 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 79.58 MPa @Strain 3.15 %, Temperature 120 °C | 11540 psi @Strain 3.15 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 80.06 MPa @Strain 6.74 %, Temperature 120 °C | 11610 psi @Strain 6.74 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 80.14 MPa @Strain 0.850 %, Temperature 0.000 °C | 11620 psi @Strain 0.850 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 80.15 MPa @Strain 9.51 %, Temperature 180 °C | 11620 psi @Strain 9.51 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 80.35 MPa @Strain 2.35 %, Temperature 90.0 °C | 11650 psi @Strain 2.35 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 80.37 MPa @Strain 9.23 %, Temperature 120 °C | 11660 psi @Strain 9.23 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 80.37 MPa @Strain 1.29 %, Temperature 60.0 °C | 11660 psi @Strain 1.29 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 80.51 MPa @Strain 1.96 %, Temperature 40.0 °C | 11680 psi @Strain 1.96 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 80.61 MPa @Strain 7.31 %, Temperature 120 °C | 11690 psi @Strain 7.31 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 80.83 MPa @Strain 10.13 %, Temperature 180 °C | 11720 psi @Strain 10.13 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 80.93 MPa @Strain 11.56 %, Temperature 180 °C | 11740 psi @Strain 11.56 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 80.98 MPa @Strain 7.89 %, Temperature 120 °C | 11750 psi @Strain 7.89 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 81.1 MPa @Strain 8.54 %, Temperature 120 °C | 11800 psi @Strain 8.54 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 81.34 MPa @Strain 10.81 %, Temperature 180 °C | 11800 psi @Strain 10.81 %, Temperature 356 °F | DAM; ISO 11403-1/-2 | |||
| 82.06 MPa @Strain 5.16 %, Temperature 150 °C | 11900 psi @Strain 5.16 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 82.23 MPa @Strain 2.47 %, Temperature 60.0 °C | 11930 psi @Strain 2.47 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 82.29 MPa @Strain 3.82 %, Temperature 90.0 °C | 11940 psi @Strain 3.82 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 83.25 MPa @Strain 0.950 %, Temperature 0.000 °C | 12070 psi @Strain 0.950 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 83.98 MPa @Strain 3.55 %, Temperature 120 °C | 12180 psi @Strain 3.55 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 84.11 MPa @Strain 5.70 %, Temperature 150 °C | 12200 psi @Strain 5.70 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 84.53 MPa @Strain 4.21 %, Temperature 90.0 °C | 12260 psi @Strain 4.21 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 85.8 MPa @Strain 1.68 %, Temperature 23.0 °C | 12400 psi @Strain 1.68 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 85.94 MPa @Strain 6.24 %, Temperature 150 °C | 12460 psi @Strain 6.24 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 86.26 MPa @Strain 4.70 %, Temperature 90.0 °C | 12510 psi @Strain 4.70 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 86.59 MPa @Strain 2.67 %, Temperature 90.0 °C | 12560 psi @Strain 2.67 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 87.0 MPa @Strain 2.23 %, Temperature 40.0 °C | 12600 psi @Strain 2.23 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 87.19 MPa @Strain 2.79 %, Temperature 60.0 °C | 12650 psi @Strain 2.79 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 87.27 MPa @Strain 0.900 %, Temperature -20.0 °C | 12660 psi @Strain 0.900 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 87.38 MPa @Strain 6.78 %, Temperature 150 °C | 12670 psi @Strain 6.78 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 87.57 MPa @Strain 5.21 %, Temperature 90.0 °C | 12700 psi @Strain 5.21 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 87.86 MPa @Strain 3.96 %, Temperature 120 °C | 12740 psi @Strain 3.96 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 88.21 MPa @Strain 1.00 %, Temperature 40.0 °C | 12790 psi @Strain 1.00 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 88.31 MPa @Strain 1.49 %, Temperature 60.0 °C | 12810 psi @Strain 1.49 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 88.62 MPa @Strain 5.77 %, Temperature 90.0 °C | 12850 psi @Strain 5.77 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 88.68 MPa @Strain 7.35 %, Temperature 150 °C | 12860 psi @Strain 7.35 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 88.72 MPa @Strain 8.83 %, Temperature 90.0 °C | 12870 psi @Strain 8.83 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 88.98 MPa @Strain 0.870 %, Temperature -20.0 °C | 12910 psi @Strain 0.870 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 89.3 MPa @Strain 6.30 %, Temperature 90.0 °C | 13000 psi @Strain 6.30 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 89.72 MPa @Strain 7.99 %, Temperature 150 °C | 13010 psi @Strain 7.99 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 89.73 MPa @Strain 6.86 %, Temperature 90.0 °C | 13010 psi @Strain 6.86 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 89.93 MPa @Strain 8.06 %, Temperature 90.0 °C | 13040 psi @Strain 8.06 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 89.96 MPa @Strain 7.44 %, Temperature 90.0 °C | 13050 psi @Strain 7.44 %, Temperature 194 °F | 50%RH; ISO 11403-1/-2 | |||
| 90.03 MPa @Strain 0.940 %, Temperature 23.0 °C | 13060 psi @Strain 0.940 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 90.54 MPa @Strain 10.61 %, Temperature 150 °C | 13130 psi @Strain 10.61 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 90.56 MPa @Strain 8.63 %, Temperature 150 °C | 13130 psi @Strain 8.63 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 91.05 MPa @Strain 4.40 %, Temperature 120 °C | 13210 psi @Strain 4.40 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 91.17 MPa @Strain 9.27 %, Temperature 150 °C | 13220 psi @Strain 9.27 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 91.41 MPa @Strain 3.16 %, Temperature 60.0 °C | 13260 psi @Strain 3.16 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 91.53 MPa @Strain 9.89 %, Temperature 150 °C | 13280 psi @Strain 9.89 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 92.05 MPa @Strain 0.980 %, Temperature 0.000 °C | 13350 psi @Strain 0.980 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 92.35 MPa @Strain 3.01 %, Temperature 90.0 °C | 13390 psi @Strain 3.01 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 93.11 MPa @Strain 2.52 %, Temperature 40.0 °C | 13500 psi @Strain 2.52 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 93.11 MPa @Strain 1.09 %, Temperature 0.000 °C | 13500 psi @Strain 1.09 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 93.19 MPa @Strain 1.92 %, Temperature 23.0 °C | 13520 psi @Strain 1.92 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 93.71 MPa @Strain 4.88 %, Temperature 120 °C | 13590 psi @Strain 4.88 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 94.77 MPa @Strain 3.51 %, Temperature 60.0 °C | 13750 psi @Strain 3.51 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 95.72 MPa @Strain 1.69 %, Temperature 60.0 °C | 13880 psi @Strain 1.69 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 95.92 MPa @Strain 5.41 %, Temperature 120 °C | 13910 psi @Strain 5.41 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 97.46 MPa @Strain 3.97 %, Temperature 60.0 °C | 14140 psi @Strain 3.97 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 97.59 MPa @Strain 3.38 %, Temperature 90.0 °C | 14150 psi @Strain 3.38 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 97.67 MPa @Strain 5.95 %, Temperature 120 °C | 14170 psi @Strain 5.95 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 97.99 MPa @Strain 1.14 %, Temperature 40.0 °C | 14210 psi @Strain 1.14 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 98.65 MPa @Strain 2.85 %, Temperature 40.0 °C | 14310 psi @Strain 2.85 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 99.12 MPa @Strain 6.53 %, Temperature 120 °C | 14380 psi @Strain 6.53 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 99.37 MPa @Strain 4.45 %, Temperature 60.0 °C | 14410 psi @Strain 4.45 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 100.07 MPa @Strain 2.16 %, Temperature 23.0 °C | 14514 psi @Strain 2.16 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 100.19 MPa @Strain 7.10 %, Temperature 120 °C | 14531 psi @Strain 7.10 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 100.25 MPa @Strain 1.04 %, Temperature -20.0 °C | 14540 psi @Strain 1.04 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 100.71 MPa @Strain 1.00 %, Temperature -20.0 °C | 14607 psi @Strain 1.00 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 100.72 MPa @Strain 5.00 %, Temperature 60.0 °C | 14608 psi @Strain 5.00 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 100.75 MPa @Strain 1.06 %, Temperature 23.0 °C | 14613 psi @Strain 1.06 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 100.86 MPa @Strain 8.16 %, Temperature 60.0 °C | 14629 psi @Strain 8.16 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 101.01 MPa @Strain 7.69 %, Temperature 120 °C | 14650 psi @Strain 7.69 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 101.08 MPa @Strain 9.73 %, Temperature 120 °C | 14660 psi @Strain 9.73 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 101.58 MPa @Strain 8.31 %, Temperature 120 °C | 14733 psi @Strain 8.31 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 101.6 MPa @Strain 5.54 %, Temperature 60.0 °C | 14740 psi @Strain 5.54 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 101.86 MPa @Strain 8.99 %, Temperature 120 °C | 14774 psi @Strain 8.99 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 102.06 MPa @Strain 6.11 %, Temperature 60.0 °C | 14803 psi @Strain 6.11 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 102.1 MPa @Strain 7.38 %, Temperature 60.0 °C | 14810 psi @Strain 7.38 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 102.11 MPa @Strain 3.76 %, Temperature 90.0 °C | 14810 psi @Strain 3.76 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 102.25 MPa @Strain 6.72 %, Temperature 60.0 °C | 14830 psi @Strain 6.72 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 102.71 MPa @Strain 1.25 %, Temperature 0.000 °C | 14897 psi @Strain 1.25 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 102.81 MPa @Strain 1.90 %, Temperature 60.0 °C | 14911 psi @Strain 1.90 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 103.12 MPa @Strain 3.13 %, Temperature 40.0 °C | 14956 psi @Strain 3.13 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 104.22 MPa @Strain 1.13 %, Temperature 0.000 °C | 15116 psi @Strain 1.13 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 105.81 MPa @Strain 4.17 %, Temperature 90.0 °C | 15346 psi @Strain 4.17 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 106.73 MPa @Strain 2.43 %, Temperature 23.0 °C | 15480 psi @Strain 2.43 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 106.74 MPa @Strain 3.51 %, Temperature 40.0 °C | 15481 psi @Strain 3.51 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 107.36 MPa @Strain 1.28 %, Temperature 40.0 °C | 15571 psi @Strain 1.28 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 108.65 MPa @Strain 4.63 %, Temperature 90.0 °C | 15758 psi @Strain 4.63 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 109.44 MPa @Strain 2.13 %, Temperature 60.0 °C | 15873 psi @Strain 2.13 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 109.47 MPa @Strain 3.97 %, Temperature 40.0 °C | 15877 psi @Strain 3.97 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 110.84 MPa @Strain 5.15 %, Temperature 90.0 °C | 16076 psi @Strain 5.15 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 110.95 MPa @Strain 1.20 %, Temperature 23.0 °C | 16092 psi @Strain 1.20 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 111.32 MPa @Strain 4.47 %, Temperature 40.0 °C | 16146 psi @Strain 4.47 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 111.47 MPa @Strain 7.56 %, Temperature 40.0 °C | 16167 psi @Strain 7.56 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 111.96 MPa @Strain 1.41 %, Temperature 0.000 °C | 16238 psi @Strain 1.41 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 112.15 MPa @Strain 1.15 %, Temperature -20.0 °C | 16266 psi @Strain 1.15 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 112.39 MPa @Strain 5.71 %, Temperature 90.0 °C | 16301 psi @Strain 5.71 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 112.46 MPa @Strain 2.70 %, Temperature 23.0 °C | 16311 psi @Strain 2.70 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 112.47 MPa @Strain 4.99 %, Temperature 40.0 °C | 16312 psi @Strain 4.99 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 112.92 MPa @Strain 1.19 %, Temperature -20.0 °C | 16378 psi @Strain 1.19 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 112.99 MPa @Strain 6.79 %, Temperature 40.0 °C | 16388 psi @Strain 6.79 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 113.07 MPa @Strain 5.57 %, Temperature 40.0 °C | 16399 psi @Strain 5.57 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 113.2 MPa @Strain 6.16 %, Temperature 40.0 °C | 16420 psi @Strain 6.16 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 113.52 MPa @Strain 8.77 %, Temperature 90.0 °C | 16465 psi @Strain 8.77 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 113.53 MPa @Strain 6.28 %, Temperature 90.0 °C | 16466 psi @Strain 6.28 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 114.2 MPa @Strain 6.86 %, Temperature 90.0 °C | 16560 psi @Strain 6.86 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 114.54 MPa @Strain 7.43 %, Temperature 90.0 °C | 16613 psi @Strain 7.43 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 114.57 MPa @Strain 8.07 %, Temperature 90.0 °C | 16617 psi @Strain 8.07 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 115.65 MPa @Strain 2.36 %, Temperature 60.0 °C | 16774 psi @Strain 2.36 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 115.93 MPa @Strain 1.27 %, Temperature 0.000 °C | 16814 psi @Strain 1.27 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 116.6 MPa @Strain 1.44 %, Temperature 40.0 °C | 16910 psi @Strain 1.44 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 117.5 MPa @Strain 2.99 %, Temperature 23.0 °C | 17040 psi @Strain 2.99 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 120.69 MPa @Strain 1.58 %, Temperature 0.000 °C | 17505 psi @Strain 1.58 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 120.82 MPa @Strain 1.34 %, Temperature 23.0 °C | 17523 psi @Strain 1.34 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 121.57 MPa @Strain 2.62 %, Temperature 60.0 °C | 17632 psi @Strain 2.62 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 121.77 MPa @Strain 3.33 %, Temperature 23.0 °C | 17661 psi @Strain 3.33 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 123.16 MPa @Strain 1.29 %, Temperature -20.0 °C | 17863 psi @Strain 1.29 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 124.92 MPa @Strain 3.74 %, Temperature 23.0 °C | 18118 psi @Strain 3.74 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 125.19 MPa @Strain 6.64 %, Temperature 23.0 °C | 18157 psi @Strain 6.64 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 125.52 MPa @Strain 1.61 %, Temperature 40.0 °C | 18205 psi @Strain 1.61 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 125.53 MPa @Strain 1.34 %, Temperature -20.0 °C | 18207 psi @Strain 1.34 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 126.8 MPa @Strain 4.19 %, Temperature 23.0 °C | 18390 psi @Strain 4.19 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 126.96 MPa @Strain 2.88 %, Temperature 60.0 °C | 18414 psi @Strain 2.88 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 127.26 MPa @Strain 1.42 %, Temperature 0.000 °C | 18458 psi @Strain 1.42 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 127.34 MPa @Strain 5.84 %, Temperature 23.0 °C | 18469 psi @Strain 5.84 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 127.74 MPa @Strain 4.69 %, Temperature 23.0 °C | 18527 psi @Strain 4.69 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 127.89 MPa @Strain 5.21 %, Temperature 23.0 °C | 18549 psi @Strain 5.21 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 129.24 MPa @Strain 1.77 %, Temperature 0.000 °C | 18745 psi @Strain 1.77 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 130.55 MPa @Strain 1.47 %, Temperature 23.0 °C | 18935 psi @Strain 1.47 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 131.69 MPa @Strain 3.16 %, Temperature 60.0 °C | 19100 psi @Strain 3.16 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 133.86 MPa @Strain 1.44 %, Temperature -20.0 °C | 19415 psi @Strain 1.44 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 134.2 MPa @Strain 1.80 %, Temperature 40.0 °C | 19460 psi @Strain 1.80 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 135.67 MPa @Strain 3.48 %, Temperature 60.0 °C | 19677 psi @Strain 3.48 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 137.27 MPa @Strain 1.96 %, Temperature 0.000 °C | 19909 psi @Strain 1.96 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 137.8 MPa @Strain 1.50 %, Temperature -20.0 °C | 19990 psi @Strain 1.50 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 137.85 MPa @Strain 1.58 %, Temperature 0.000 °C | 19993 psi @Strain 1.58 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 138.55 MPa @Strain 3.83 %, Temperature 60.0 °C | 20095 psi @Strain 3.83 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 140.13 MPa @Strain 1.63 %, Temperature 23.0 °C | 20324 psi @Strain 1.63 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 140.19 MPa @Strain 5.69 %, Temperature 60.0 °C | 20333 psi @Strain 5.69 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 140.3 MPa @Strain 4.20 %, Temperature 60.0 °C | 20350 psi @Strain 4.20 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 141.03 MPa @Strain 4.65 %, Temperature 60.0 °C | 20455 psi @Strain 4.65 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 141.07 MPa @Strain 5.15 %, Temperature 60.0 °C | 20461 psi @Strain 5.15 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 142.42 MPa @Strain 2.00 %, Temperature 40.0 °C | 20656 psi @Strain 2.00 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 144.3 MPa @Strain 1.60 %, Temperature -20.0 °C | 20930 psi @Strain 1.60 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 144.92 MPa @Strain 2.15 %, Temperature 0.000 °C | 21019 psi @Strain 2.15 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 148.36 MPa @Strain 1.73 %, Temperature 0.000 °C | 21518 psi @Strain 1.73 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 149.76 MPa @Strain 1.79 %, Temperature 23.0 °C | 21721 psi @Strain 1.79 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 149.76 MPa @Strain 1.65 %, Temperature -20.0 °C | 21721 psi @Strain 1.65 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 149.76 MPa @Strain 2.22 %, Temperature 40.0 °C | 21721 psi @Strain 2.22 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 152.17 MPa @Strain 2.36 %, Temperature 0.000 °C | 22070 psi @Strain 2.36 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 154.71 MPa @Strain 1.78 %, Temperature -20.0 °C | 22439 psi @Strain 1.78 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 156.76 MPa @Strain 2.47 %, Temperature 40.0 °C | 22736 psi @Strain 2.47 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 158.44 MPa @Strain 1.96 %, Temperature 23.0 °C | 22980 psi @Strain 1.96 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 158.72 MPa @Strain 1.90 %, Temperature 0.000 °C | 23020 psi @Strain 1.90 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 158.91 MPa @Strain 2.60 %, Temperature 0.000 °C | 23048 psi @Strain 2.60 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 161.42 MPa @Strain 1.82 %, Temperature -20.0 °C | 23412 psi @Strain 1.82 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 162.66 MPa @Strain 2.73 %, Temperature 40.0 °C | 23592 psi @Strain 2.73 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 164.55 MPa @Strain 1.96 %, Temperature -20.0 °C | 23866 psi @Strain 1.96 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 164.99 MPa @Strain 2.86 %, Temperature 0.000 °C | 23930 psi @Strain 2.86 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 167.18 MPa @Strain 2.15 %, Temperature 23.0 °C | 24247 psi @Strain 2.15 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 167.55 MPa @Strain 3.03 %, Temperature 40.0 °C | 24301 psi @Strain 3.03 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 168.26 MPa @Strain 2.06 %, Temperature 0.000 °C | 24404 psi @Strain 2.06 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 168.73 MPa @Strain 4.51 %, Temperature 0.000 °C | 24472 psi @Strain 4.51 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 169.22 MPa @Strain 4.33 %, Temperature 40.0 °C | 24543 psi @Strain 4.33 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 169.8 MPa @Strain 3.10 %, Temperature 0.000 °C | 24630 psi @Strain 3.10 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 170.95 MPa @Strain 3.37 %, Temperature 40.0 °C | 24794 psi @Strain 3.37 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 171.75 MPa @Strain 3.78 %, Temperature 40.0 °C | 24910 psi @Strain 3.78 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 172.75 MPa @Strain 3.45 %, Temperature 0.000 °C | 25055 psi @Strain 3.45 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 172.81 MPa @Strain 3.90 %, Temperature 0.000 °C | 25064 psi @Strain 3.90 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 172.92 MPa @Strain 1.99 %, Temperature -20.0 °C | 25080 psi @Strain 1.99 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 173.55 MPa @Strain 2.14 %, Temperature -20.0 °C | 25171 psi @Strain 2.14 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 175.47 MPa @Strain 2.36 %, Temperature 23.0 °C | 25450 psi @Strain 2.36 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 177.77 MPa @Strain 2.25 %, Temperature 0.000 °C | 25783 psi @Strain 2.25 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 182.38 MPa @Strain 2.34 %, Temperature -20.0 °C | 26452 psi @Strain 2.34 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 182.64 MPa @Strain 2.57 %, Temperature 23.0 °C | 26490 psi @Strain 2.57 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 184.06 MPa @Strain 2.16 %, Temperature -20.0 °C | 26696 psi @Strain 2.16 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 187.04 MPa @Strain 2.44 %, Temperature 0.000 °C | 27128 psi @Strain 2.44 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 188.74 MPa @Strain 2.79 %, Temperature 23.0 °C | 27374 psi @Strain 2.79 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 190.33 MPa @Strain 2.55 %, Temperature -20.0 °C | 27605 psi @Strain 2.55 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 194.24 MPa @Strain 3.06 %, Temperature 23.0 °C | 28172 psi @Strain 3.06 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 194.97 MPa @Strain 2.35 %, Temperature -20.0 °C | 28278 psi @Strain 2.35 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 195.89 MPa @Strain 2.67 %, Temperature 0.000 °C | 28411 psi @Strain 2.67 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 197.8 MPa @Strain 2.79 %, Temperature -20.0 °C | 28690 psi @Strain 2.79 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 198.07 MPa @Strain 3.36 %, Temperature 23.0 °C | 28728 psi @Strain 3.36 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 198.13 MPa @Strain 3.76 %, Temperature 23.0 °C | 28736 psi @Strain 3.76 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 203.83 MPa @Strain 2.85 %, Temperature 0.000 °C | 29563 psi @Strain 2.85 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 204.4 MPa @Strain 3.01 %, Temperature -20.0 °C | 29650 psi @Strain 3.01 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 205.39 MPa @Strain 2.54 %, Temperature -20.0 °C | 29789 psi @Strain 2.54 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 209.18 MPa @Strain 3.30 %, Temperature -20.0 °C | 30339 psi @Strain 3.30 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 209.99 MPa @Strain 3.76 %, Temperature -20.0 °C | 30457 psi @Strain 3.76 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 211.05 MPa @Strain 3.11 %, Temperature 0.000 °C | 30610 psi @Strain 3.11 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 215.39 MPa @Strain 2.71 %, Temperature -20.0 °C | 31240 psi @Strain 2.71 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 217.05 MPa @Strain 3.43 %, Temperature 0.000 °C | 31480 psi @Strain 3.43 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 220.26 MPa @Strain 3.83 %, Temperature 0.000 °C | 31946 psi @Strain 3.83 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 224.73 MPa @Strain 2.90 %, Temperature -20.0 °C | 32594 psi @Strain 2.90 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 233.72 MPa @Strain 3.13 %, Temperature -20.0 °C | 33898 psi @Strain 3.13 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 242.1 MPa @Strain 3.38 %, Temperature -20.0 °C | 35110 psi @Strain 3.38 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 249.74 MPa @Strain 3.63 %, Temperature -20.0 °C | 36222 psi @Strain 3.63 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| Elongation at Break | 3.5 % @Temperature 23.0 °C | 3.5 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 5.8 % @Temperature 23.0 °C | 5.8 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 7.20 GPa @Temperature 23.0 °C | 1040 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 9.70 GPa @Temperature 23.0 °C | 1410 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Charpy Impact Unnotched | 8.60 J/cm² @Temperature 23.0 °C | 40.9 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | ||
| 9.30 J/cm² @Temperature 23.0 °C | 44.3 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.10 J/cm² @Temperature 23.0 °C | 5.23 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
| 1.30 J/cm² @Temperature 23.0 °C | 6.19 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature 23.0 - 55.0 °C | 55.6 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 290 °C | 554 °F | DAM; Optimum | |||
| 280 - 300 °C | 536 - 572 °F | DAM | |||
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM | ||
| 100 °C | 212 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Appearance | Black Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Features | Hydrolysis Resistant | DAM | |||
| Filler | Glass Reinforced | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Material Status | Preliminary Data | DAM | |||
| Part Marking Code | >PA66-GF30< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA66 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Glass Reinforced Resins | DAM | |||
| SHIELD Technology Resins | DAM | ||||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA66-GF30 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Ultrasonic Weldable | Yes | DAM | |||
| Uses | Automotive Applications | DAM | |||
| Automotive Under the Hood | DAM | ||||
| Tanks | DAM | ||||