- 密度 [g/cm3]: 1.09
- 拉伸强度 [MPa]: 51.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | DAM; ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.018 cm/cm @Thickness 2.00 mm | 0.018 in/in @Thickness 0.0787 in | DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm @Thickness 2.00 mm | 0.018 in/in @Thickness 0.0787 in | DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 51.0 MPa @Temperature 23.0 °C | 7400 psi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Elongation at Break | 38 % @Temperature 23.0 °C | 38 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| Elongation at Yield | 6.0 % @Temperature 23.0 °C | 6.0 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| Tensile Modulus | 2.003 GPa @Temperature 23.0 °C | 290.5 ksi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Charpy Impact Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | DAM; ISO 179/1eU | ||
| Charpy Impact, Notched | 7.20 J/cm² @Temperature 23.0 °C | 34.3 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 110 µm/m-°C @Temperature 23.0 - 55.0 °C | 61.1 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 120 µm/m-°C @Temperature 23.0 - 55.0 °C | 66.7 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | ||
| Melting Point | 263 °C | 505 °F | DAM; 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | DAM; ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | DAM; IEC 60695-11-10 | ||
| HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | DAM; UL94 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 290 °C | 554 °F | DAM; optimum | ||
| 280 - 300 °C | 536 - 572 °F | DAM | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; Optimum | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM; Dehumidified Dryer | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Appearance | Black Color | ||||
| Forms | Pellets | ||||
| Generic | Nylon 66 | ||||
| Material Status | Preliminary Data | ||||
| Part Marking Code | >PA66-HI< | ISO 11469 | |||
| Processing Method | injection Molding | ||||
| Product Category | Toughened Resins | ||||
| Region Available - Americas | Yes | ||||
| Resin Identification | PA66-HI | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||