- 密度 [g/cm3]: 1.23
- 吸水率 [%]: 1.4
- 缺口冲击强度: 0.43
- 弯曲强度 [MPa]: 118.0
- 弯曲模量 [MPa]: 4.94
- 硬度: 121.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 | ||
| Water Absorption | 1.4 % | 1.4 % | 24 hour; ISO Test | ||
| 8.1 % | 8.1 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.3 % | 2.3 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Measurement | 50 | 50 | Formic Acid | ||
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 121 | 121 | ASTM Test | ||
| Tensile Strength at Break | 118 MPa | 17100 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 118 MPa | 17100 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 2.9 % | 2.9 % | 0.2 in/min; ASTM Test | ||
| Flexural Modulus | 4.94 GPa | 716 ksi | ASTM Test | ||
| 5.10 GPa | 740 ksi | ISO Data | |||
| Izod Impact, Notched | 0.430 J/cm @Thickness 3.17 mm | 0.806 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Izod Impact, Notched (ISO) | 3.80 kJ/m² | 1.81 ft-lb/in² | ISO Test | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 50.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 27.8 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | ISO 75 | ||
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Descriptive Properties | |||||
| Color | BK-106 | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| UL.UL-C | Yes | ||||