- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 1.6
- 缺口冲击强度: 0.32
- 拉伸强度 [MPa]: 88.0
- 弯曲模量 [MPa]: 2.80
- 硬度: 120.0
- 热变形温度 [℃]: 165.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 | ||
| Water Absorption | 1.6 % | 1.6 % | 24 hour; ISO Test | ||
| 9.3 % | 9.3 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.6 % | 2.6 % | 23°C/50% R.H.; ISO 62 | ||
| Relative Viscosity | 2.6 cP | 2.6 cP | ISO Test; 96 % SAV | ||
| Viscosity Measurement | 48 | 48 | Formic Acid | ||
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 120 | 120 | ASTM Test | ||
| Tensile Strength at Break | 90.0 MPa | 13100 psi | 0.2 in/min; ASTM Test | ||
| 25.0 MPa @Temperature 120 °C | 3630 psi @Temperature 248 °F | ASTM Test | |||
| 25.0 MPa @Temperature 120 °C | 3630 psi @Temperature 248 °F | ISO Data | |||
| 35.0 MPa @Temperature 80.0 °C | 5080 psi @Temperature 176 °F | ISO Data | |||
| 35.0 MPa @Temperature 80.0 °C | 5080 psi @Temperature 176 °F | ASTM Test | |||
| 130 MPa @Temperature -40.0 °C | 18900 psi @Temperature -40.0 °F | ASTM Test | |||
| 130 MPa @Temperature -40.0 °C | 18900 psi @Temperature -40.0 °F | ISO Data | |||
| Tensile Strength, Yield | 88.0 MPa | 12800 psi | 50mm/min; ISO 527 | ||
| 90.0 MPa | 13100 psi | 2 in/min; ASTM Test | |||
| 30.0 MPa @Temperature 120 °C | 4350 psi @Temperature 248 °F | ASTM Test | |||
| 30.0 MPa @Temperature 120 °C | 4350 psi @Temperature 248 °F | ISO Data | |||
| 40.0 MPa @Temperature 80.0 °C | 5800 psi @Temperature 176 °F | ISO Data | |||
| 40.0 MPa @Temperature 80.0 °C | 5800 psi @Temperature 176 °F | ASTM Test | |||
| 137 MPa @Temperature -40.0 °C | 19900 psi @Temperature -40.0 °F | ASTM Test | |||
| 137 MPa @Temperature -40.0 °C | 19900 psi @Temperature -40.0 °F | ISO Data | |||
| Elongation at Break | 7.0 % | 7.0 % | 50mm/min, Nominal strain; ISO 527 | ||
| 12 % | 12 % | 2 in/min; ASTM Test | |||
| >= 100 % | >= 100 % | ||||
| 5.0 % @Temperature -40.0 °C | 5.0 % @Temperature -40.0 °F | ASTM Test | |||
| 5.0 % @Temperature -40.0 °C | 5.0 % @Temperature -40.0 °F | ISO Data | |||
| >= 100 % @Temperature 120 °C | >= 100 % @Temperature 248 °F | ISO Data | |||
| >= 100 % @Temperature 80.0 °C | >= 100 % @Temperature 176 °F | ISO Data | |||
| >= 100 % @Temperature 120 °C | >= 100 % @Temperature 248 °F | ASTM Test | |||
| Elongation at Yield | 4.0 % | 4.0 % | 50mm/min; ISO 527 | ||
| 4.0 % | 4.0 % | 2 in/min; ASTM Test | |||
| 3.0 % @Temperature -40.0 °C | 3.0 % @Temperature -40.0 °F | ASTM Test | |||
| 3.0 % @Temperature -40.0 °C | 3.0 % @Temperature -40.0 °F | ISO Data | |||
| 25 % @Temperature 80.0 °C | 25 % @Temperature 176 °F | ASTM Test | |||
| 25 % @Temperature 80.0 °C | 25 % @Temperature 176 °F | ISO Data | |||
| 27 % @Temperature 120 °C | 27 % @Temperature 248 °F | ASTM Test | |||
| 27 % @Temperature 120 °C | 27 % @Temperature 248 °F | ISO Data | |||
| Tensile Modulus | 3.70 GPa | 537 ksi | 1mm/min; ISO 527 | ||
| 0.550 GPa @Temperature 120 °C | 79.8 ksi @Temperature 248 °F | ISO Data | |||
| 0.750 GPa @Temperature 80.0 °C | 109 ksi @Temperature 176 °F | ISO Data | |||
| 4.09 GPa @Temperature -40.0 °C | 593 ksi @Temperature -40.0 °F | ISO Data | |||
| Flexural Strength | 95.0 MPa | 13800 psi | ISO Data | ||
| 110 MPa | 16000 psi | ASTM Test | |||
| 21.0 MPa @Temperature 120 °C | 3050 psi @Temperature 248 °F | ASTM Test | |||
| 30.0 MPa @Temperature 65.0 °C | 4350 psi @Temperature 149 °F | ASTM Test | |||
| 183 MPa @Temperature -40.0 °C | 26500 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Modulus | 2.80 GPa | 406 ksi | ISO Data | ||
| 3.17 GPa | 460 ksi | ASTM Test | |||
| 0.385 GPa @Temperature 120 °C | 55.8 ksi @Temperature 248 °F | ASTM Test | |||
| 0.440 GPa @Temperature 93.0 °C | 63.8 ksi @Temperature 199 °F | ASTM Test | |||
| 0.600 GPa @Temperature 65.0 °C | 87.0 ksi @Temperature 149 °F | ASTM Test | |||
| Izod Impact, Notched | 0.320 J/cm @Temperature -40.0 °C | 0.599 ft-lb/in @Temperature -40.0 °F | ASTM Test | ||
| 0.480 J/cm @Thickness 3.17 mm | 0.899 ft-lb/in @Thickness 0.125 in | ASTM Test | |||
| Charpy Impact Unnotched | NB | NB | ISO 179 | ||
| Charpy Impact, Notched | 0.350 J/cm² | 1.67 ft-lb/in² | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 81.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 45.0 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75 | ||
| 190 °C | 374 °F | ASTM Test | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ISO 75 | ||
| 75.0 °C | 167 °F | ASTM Test | |||
| Flammability, UL94 | V-2 @Thickness 0.700 mm | V-2 @Thickness 0.0276 in | |||
| V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 °C | 500 °F | Injection molding | ||
| Mold Temperature | 80.0 °C | 176 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| UL.UL-C | Yes | ||||