- 密度 [g/cm3]: 1.62
- 吸水率 [%]: 4.0
- 缺口冲击强度: 0.8
- 弯曲强度 [MPa]: 145.0
- 弯曲模量 [MPa]: 9.17
- 硬度: 121.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in³ | ISO 1183 | ||
| Water Absorption | 4.0 % | 4.0 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.1 % | 1.1 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Measurement | 50 | 50 | Formic Acid | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 121 | 121 | ASTM Test | ||
| Tensile Strength at Break | 145 MPa | 21000 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 145 MPa | 21000 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 2.5 % | 2.5 % | 5mm/min; ISO 527 | ||
| 2.5 % | 2.5 % | 0.2 in/min; ASTM Test | |||
| Flexural Strength | 210 MPa | 30500 psi | ASTM Test | ||
| Flexural Modulus | 9.17 GPa | 1330 ksi | ASTM Test | ||
| Izod Impact, Notched | 0.800 J/cm @Thickness 3.17 mm | 1.50 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ASTM Test | ||
| Flammability, UL94 | V-0 @Thickness 0.840 mm | V-0 @Thickness 0.0331 in | |||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | ||||
| 5VA @Thickness 2.50 mm | 5VA @Thickness 0.0984 in | ||||
| Descriptive Properties | |||||
| Color | BK-102 | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| UL.UL-C | Yes | ||||