- 密度 [g/cm3]: 1.106
- 弯曲模量 [MPa]: 4.647
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.106 g/cc | 0.03996 lb/in³ | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 76.10 MPa | 11040 psi | UNI EN ISO 527-1(97) and UNI EN ISO 527-2(97) | ||
| Elongation at Break | 11.38 % | 11.38 % | UNI EN ISO 527-1(97) and UNI EN ISO 527-2(97) | ||
| Tensile Modulus | 6.2196 GPa | 902.09 ksi | UNI EN ISO 527-1(97) and UNI EN ISO 527-2(97) | ||
| Flexural Strength | 120.08 MPa | 17416 psi | UNI EN ISO 14125: 2000 | ||
| Flexural Modulus | 4.647 GPa | 674.1 ksi | UNI EN ISO 14125: 2000 | ||
| Charpy Impact Unnotched | 2.868 J/cm² | 13.65 ft-lb/in² | ISO 179-1:2007 | ||
| Charpy Impact, Notched | 0.582 J/cm² | 2.77 ft-lb/in² | ISO 179-1:2007 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | <= 1e+8 ohm-cm | <= 1e+8 ohm-cm | ASTM D257-93 | ||
| Surface Resistance | <= 1e+8 ohm | <= 1e+8 ohm | ASTM D257-93 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 193.3 °C | 379.9 °F | ISO 11357-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 185.6 °C | 366.1 °F | ASTM D648 Type B | ||
| Vicat Softening Point | 189.9 °C | 373.8 °F | 10 N; ASTM D1525-09 | ||
| Descriptive Properties | |||||
| Color | Deep Black | ||||
| Surface Finish | 1.15 Ra µm | After CNC Machining | |||
| 1.45 Ra µm | After Manual Finishing | ||||
| 6.2 Ra µm | After SLS Process | ||||