- 熔体流动速率 [g/10min]: 14.0
- 密度 [g/cm3]: 1.02
- 拉伸强度 [MPa]: 25.0
- 热变形温度 [℃]: 73.0
- 透光率 [%]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | |
| Melt Flow | 14 g/10 min @Load 2.16 kg, Temperature 235 °C | 14 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 28 % | 28 % | 50 mm/min |
| Tensile Modulus | 0.405 GPa | 58.7 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB | NB | Low Temp | |
| Charpy Impact, Notched | NB | NB | |
| 1.22 J/cm² @Temperature -30.0 °C | 5.81 ft-lb/in² @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | |
| Surface Resistance | 4.00e+14 ohm | 4.00e+14 ohm | |
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature 20.0 °C | 50.0 µin/in-°F @Temperature 68.0 °F | |
| Melting Point | 171 °C | 340 °F | (Dry) |
| Deflection Temperature at 0.46 MPa (66 psi) | 73.0 °C | 163 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 40.0 °C | 104 °F | |
| Vicat Softening Point | 180 °C | 356 °F | 50°C/hr; 50N |
| Flammability, UL94 | V-2 @Thickness 3.20 mm | V-2 @Thickness 0.126 in | |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 80 % | 80 % | Mfr. reports 'Transparent' but doesn't quantify. |