- 熔体流动速率 [g/10min]: 1.5
- 密度 [g/cm3]: 1.05
- 拉伸强度 [MPa]: 15.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | |
| Melt Flow | 1.5 g/10 min @Load 2.16 kg, Temperature 235 °C | 1.5 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 15.0 MPa @Strain 50.0 % | 2180 psi @Strain 50.0 % | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Tensile Modulus | 0.170 GPa | 24.7 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB | NB | Low Temp | |
| Charpy Impact, Notched | NB | NB | |
| 0.330 J/cm² @Temperature -30.0 °C | 1.57 ft-lb/in² @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 5.00e+9 ohm-cm | 5.00e+9 ohm-cm | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 150 µm/m-°C @Temperature 20.0 °C | 83.3 µin/in-°F @Temperature 68.0 °F | |
| Melting Point | 170 °C | 338 °F | (Dry) |
| Vicat Softening Point | 95.0 °C | 203 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.10 mm | HB @Thickness 0.122 in | ||