- 密度 [g/cm3]: 1.14
- 缺口冲击强度: 7.0
- 拉伸强度 [MPa]: 45.0
- 断裂伸长率 [%]: 54.0
- 弯曲模量 [MPa]: 1.90
- 热变形温度 [℃]: 174.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.011 cm/cm | 0.011 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 42.0 MPa | 6090 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 5 mm/min; ISO 527 |
| Elongation at Yield | 17 % | 17 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 1.40 GPa | 203 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 54.0 MPa | 7830 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.90 GPa | 276 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 44.4 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 140 µm/m-°C @Temperature 23.0 - 60.0 °C | 77.8 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 174 °C | 345 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 72.0 °C | 162 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |