LNP Thermocomp® HF-1006 Polyamide 11, Glass Fiber Reinforcement

LNP Thermocomp® HF-1006 Polyamide 11, Glass Fiber Reinforcement 物性表: LNP Thermocomp® HF-1006 Polyamide 11, Glass Fiber Reinforcement物性表及特性介绍,LNP Thermocomp® HF-1006 Polyamide 11, Glass Fiber Reinforcement注塑参数详情,如需LNP Thermocomp® HF-1006 Polyamide 11, Glass Fiber Reinforcement下载, 可到相关下载区下载
  • 吸水率 [%]: 0.1
  • 缺口冲击强度: 2.56
  • 拉伸强度 [MPa]: 134.0
  • 弯曲模量 [MPa]: 6.21
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.26 g/cc1.26 g/ccMethod A; ASTM D792
Water Absorption 0.10 %0.10 %at 24 hrs; ASTM D570
Linear Mold Shrinkage 0.0010 - 0.0020 cm/cm0.0010 - 0.0020 in/inASTM D955
Linear Mold Shrinkage, Transverse 0.0060 - 0.0070 cm/cm0.0060 - 0.0070 in/inASTM D955
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 134 MPa19400 psiASTM D638
Tensile Strength, Yield 134 MPa19400 psiASTM D638
Elongation at Break 6.2 %6.2 %ASTM D638
Elongation at Yield 5.3 %5.3 %ASTM D638
Tensile Modulus 7.38 GPa1070 ksiASTM D638
Flexural Strength 193 MPa28000 psiASTM D790
Flexural Modulus 6.21 GPa901 ksiASTM D790
Izod Impact, Notched 2.56 J/cm
@Thickness 3.18 mm
4.80 ft-lb/in
@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 14.3 J/cm
@Thickness 3.18 mm
26.8 ft-lb/in
@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 25.3 kJ/m²12.0 ft-lb/in²ISO 180
Izod Impact, Unnotched (ISO) 87.8 kJ/m²41.8 ft-lb/in²ISO 180
Falling Dart Impact 16.7 J12.3 ft-lbASTM D3763
Impact Test 6.72 J4.96 ft-lbMulti-Axial Instrumented Impact Energy; ISO 6603-2
 
Thermal PropertiesMetricEnglishComments
CTE, linear 34.0 µm/m-°C
@Temperature 20.0 °C
18.9 µin/in-°F
@Temperature 68.0 °F
TMA; ASTM E831
CTE, linear, Transverse to Flow 99.0 µm/m-°C
@Temperature 20.0 °C
55.0 µin/in-°F
@Temperature 68.0 °F
TMA; ASTM E831
Deflection Temperature at 1.8 MPa (264 psi) 178 °C352 °FUnannealed; ASTM D648
 
Processing PropertiesMetricEnglishComments
Melt Temperature 227 - 260 °C441 - 500 °F
Mold Temperature 43.3 - 51.7 °C110 - 125 °F
Drying Temperature 82.2 °C180 °F
Dry Time 4 hour4 hour
Moisture Content 0.15 %0.15 %Suggested
Back Pressure 0.172 - 0.345 MPa24.9 - 50.0 psi

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-47444.html

免责声明: 本文 LNP Thermocomp® HF-1006 Polyamide 11, Glass Fiber Reinforcement 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4