- 拉伸强度 [MPa]: 41.0
- 断裂伸长率 [%]: 12.0
- 弯曲模量 [MPa]: 0.300
- 热变形温度 [℃]: 120.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage, Flow | 0.026 cm/cm | 0.026 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 41.0 MPa | 5950 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 225 % | 225 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 115 % | 115 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 1.20 GPa | 174 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 12.0 MPa | 1740 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 0.300 GPa | 43.5 ksi | 2 mm/min; ISO 178 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 210 µm/m-°C @Temperature 23.0 - 60.0 °C | 117 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 190 µm/m-°C @Temperature 23.0 - 60.0 °C | 106 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 48.0 °C | 118 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |