- 缺口冲击强度: 0.907
- 弯曲模量 [MPa]: 8.62
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | Method A; ASTM D792 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 137 MPa | 19900 psi | ASTM D638 |
| Elongation at Break | 2.8 % | 2.8 % | ASTM D638 |
| Flexural Strength | 207 MPa | 30000 psi | ASTM D790 |
| Flexural Modulus | 8.62 GPa | 1250 ksi | ASTM D790 |
| Izod Impact, Notched | 0.907 J/cm @Thickness 3.18 mm | 1.70 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Unnotched | 9.07 J/cm @Thickness 3.18 mm | 17.0 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 396 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 268 - 274 °C | 514 - 525 °F | |
| Mold Temperature | 82.2 - 93.3 °C | 180 - 200 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.20 % | 0.20 % | Suggested |
| Back Pressure | 0.172 - 0.345 MPa | 24.9 - 50.0 psi | |