- 缺口冲击强度: 1.57
- 断裂伸长率 [%]: 281
- 弯曲模量 [MPa]: 13.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.00030 - 0.0015 cm/cm @Thickness 3.20 mm | 0.00030 - 0.0015 in/in @Thickness 0.126 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Elongation at Break | 6.0 % @Thickness 3.20 mm | 6.0 % @Thickness 0.126 in | 5mm/min; ASTM D638 |
| Flexural Yield Strength | 281 MPa @Thickness 3.20 mm | 40800 psi @Thickness 0.126 in | 1.3mm/min; ASTM D790 |
| Flexural Modulus | 13.0 GPa @Thickness 3.20 mm | 1890 ksi @Thickness 0.126 in | 1.3mm/min; ASTM D790 |
| Izod Impact, Notched | 1.57 J/cm @Thickness 3.20 mm, Temperature 23.0 °C | 2.94 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Flammability, UL94 | HB @Thickness >=0.800 mm | HB @Thickness >=0.0315 in | |
| HB @Thickness >=1.60 mm | HB @Thickness >=0.0630 in | ||
| HB @Thickness >=2.50 mm | HB @Thickness >=0.0984 in | ||
| HB @Thickness >=3.20 mm | HB @Thickness >=0.126 in | ||
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 280 - 300 °C | 536 - 572 °F | Injection Molding |
| Middle Barrel Temperature | 280 - 300 °C | 536 - 572 °F | Injection Molding |
| Front Barrel Temperature | 280 - 300 °C | 536 - 572 °F | Injection Molding |
| Nozzle Temperature | 280 - 320 °C | 536 - 608 °F | Injection Molding |
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | Injection Molding |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
| Back Pressure | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| Screw Speed | 50 - 150 rpm | 50 - 150 rpm | Injection Molding |