LNP Thermotuf® QF-1006 HI Polyamide 6/10 Copolymer, Glass Fiber Reinforcement

LNP Thermotuf® QF-1006 HI Polyamide 6/10 Copolymer, Glass Fiber Reinforcement 物性表: LNP Thermotuf® QF-1006 HI Polyamide 6/10 Copolymer, Glass Fiber Reinforcement物性表及特性介绍,LNP Thermotuf® QF-1006 HI Polyamide 6/10 Copolymer, Glass Fiber Reinforcement注塑参数详情,如需LNP Thermotuf® QF-1006 HI Polyamide 6/10 Copolymer, Glass Fiber Reinforcement下载, 可到相关下载区下载
  • 吸水率 [%]: 0.2
  • 缺口冲击强度: 1.28
  • 拉伸强度 [MPa]: 140.0
  • 弯曲模量 [MPa]: 7.03
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.29 g/cc1.29 g/ccMethod A; ASTM D792
Water Absorption 0.20 %0.20 %at 24 hrs; ASTM D570
Linear Mold Shrinkage 0.0020 cm/cm0.0020 in/inASTM D955
Linear Mold Shrinkage, Transverse 0.010 cm/cm0.010 in/inASTM D955
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 140 MPa20300 psiASTM D638
Tensile Strength, Yield 140 MPa20300 psiASTM D638
Elongation at Break 3.4 %3.4 %ASTM D638
Elongation at Yield 3.3 %3.3 %ASTM D638
Tensile Modulus 8.48 GPa1230 ksiASTM D638
Flexural Strength 207 MPa30000 psiASTM D790
Flexural Modulus 7.03 GPa1020 ksiASTM D790
Izod Impact, Notched 1.28 J/cm
@Thickness 3.18 mm
2.40 ft-lb/in
@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 11.6 J/cm
@Thickness 3.18 mm
21.7 ft-lb/in
@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 15.4 kJ/m²7.33 ft-lb/in²ISO 180
Izod Impact, Unnotched (ISO) 73.4 kJ/m²34.9 ft-lb/in²ISO 180
Falling Dart Impact 9.30 J6.86 ft-lbASTM D3763
Impact Test 3.52 J2.60 ft-lbMulti-Axial Instrumented Impact Energy; ISO 6603-2
 
Thermal PropertiesMetricEnglishComments
CTE, linear 31.0 µm/m-°C
@Temperature 20.0 °C
17.2 µin/in-°F
@Temperature 68.0 °F
TMA; ASTM E831
CTE, linear, Transverse to Flow 88.0 µm/m-°C
@Temperature 20.0 °C
48.9 µin/in-°F
@Temperature 68.0 °F
TMA; ASTM E831
Deflection Temperature at 1.8 MPa (264 psi) 208 °C406 °FUnannealed; ASTM D648
 
Processing PropertiesMetricEnglishComments
Melt Temperature 268 - 274 °C514 - 525 °F
Mold Temperature 82.2 - 93.3 °C180 - 200 °F
Drying Temperature 82.2 °C180 °F
Dry Time 4 hour4 hour
Moisture Content 0.020 %0.020 %Suggested
Back Pressure 0.172 - 0.345 MPa24.9 - 50.0 psi

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-48050.html

免责声明: 本文 LNP Thermotuf® QF-1006 HI Polyamide 6/10 Copolymer, Glass Fiber Reinforcement 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4