- 密度 [g/cm3]: 1.43
- 缺口冲击强度: 0.7
- 断裂伸长率 [%]: 370
- 弯曲模量 [MPa]: 23.7
- 热变形温度 [℃]: 335.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0700 % | 0.0700 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.030 cm/cm @Time 86400 sec | 0.0010 - 0.030 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec | 0.0070 - 0.0090 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 246 MPa | 35700 psi | 5 mm/min; ISO 527 |
| 248 MPa | 36000 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 1.6 % | 1.6 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 28.35 GPa | 4112 ksi | 1 mm/min; ISO 527 |
| 28.54 GPa | 4139 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 360 MPa | 52200 psi | ISO 178 |
| 365 MPa | 52900 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 370 MPa | 53700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 23.7 GPa | 3440 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 23.8 GPa | 3450 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.700 J/cm | 1.31 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.71 J/cm | 14.4 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C | 5.16 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 9.00 µm/m-°C @Temperature -30.0 - 30.0 °C | 5.00 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| CTE, linear, Transverse to Flow | 38.9 µm/m-°C @Temperature -30.0 - 30.0 °C | 21.6 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 335 °C | 635 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 337 °C @Thickness 3.20 mm | 639 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 318 °C | 604 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 325 °C @Thickness 3.20 mm | 617 °F @Thickness 0.126 in | unannealed; ASTM D648 | |