- 密度 [g/cm3]: 1.42
- 缺口冲击强度: 0.42
- 拉伸强度 [MPa]: 114.0
- 弯曲模量 [MPa]: 6.89
- 热变形温度 [℃]: 329.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 |
| 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec | 0.0030 - 0.0050 in/in @Time 24.0 hour | ASTM D955 |
| 0.0044 cm/cm @Time 86400 sec | 0.0044 in/in @Time 24.0 hour | ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0058 cm/cm @Time 86400 sec | 0.0058 in/in @Time 24.0 hour | ISO 294 |
| 0.0050 - 0.0070 cm/cm @Time 86400 sec | 0.0050 - 0.0070 in/in @Time 24.0 hour | ASTM D955 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 114 MPa | 16500 psi | ISO 527 |
| 126 MPa | 18300 psi | ASTM D638 | |
| Tensile Strength, Yield | 114 MPa | 16500 psi | ISO 527 |
| 126 MPa | 18300 psi | ASTM D638 | |
| Elongation at Break | 1.8 % | 1.8 % | ISO 527 |
| 2.2 % | 2.2 % | ASTM D638 | |
| Elongation at Yield | 1.8 % | 1.8 % | ISO 527 |
| 2.2 % | 2.2 % | ASTM D638 | |
| Tensile Modulus | 7.58 GPa | 1100 ksi | 50 mm/min; ASTM D638 |
| 7.63 GPa | 1110 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 207 MPa | 30000 psi | ISO 178 |
| 213 MPa | 30900 psi | ASTM D790 | |
| Flexural Modulus | 6.89 GPa | 999 ksi | ASTM D790 |
| 7.00 GPa | 1020 ksi | ISO 178 | |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.23 J/cm | 9.80 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J | 5.90 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 45.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 25.0 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 45.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 25.0 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 33.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 18.3 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 34.2 µm/m-°C @Temperature -40.0 - 40.0 °C | 19.0 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 329 °C | 624 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 332 °C @Thickness 3.20 mm | 630 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 261 °C | 502 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 286 °C @Thickness 3.20 mm | 547 °F @Thickness 0.126 in | unannealed; ASTM D648 | |