- 弯曲模量 [MPa]: 3.45
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Viscosity | 17000 cP | 17000 cP | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 121 | 121 | |
| Tensile Strength at Break | 26.2 MPa | 3800 psi | |
| Elongation at Break | 0.70 % | 0.70 % | |
| Flexural Strength | 100 MPa | 14500 psi | |
| Flexural Modulus | 3.45 GPa | 500 ksi | |
| Compressive Strength | 244 MPa | 35400 psi | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.10e+16 ohm-cm | 1.10e+16 ohm-cm | C 96/23/96 |
| 1.22e+16 ohm-cm | 1.22e+16 ohm-cm | "A" | |
| Surface Resistance | >= 7.85e+15 ohm | >= 7.85e+15 ohm | Cond. A |
| >= 7.85e+15 ohm | >= 7.85e+15 ohm | C 96/23/96 | |
| Dielectric Constant | 3.33 @Frequency 1.00e+6 Hz | 3.33 @Frequency 1.00e+6 Hz | A |
| 3.57 @Frequency 60.0 Hz | 3.57 @Frequency 60.0 Hz | A | |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 0.167 - 0.201 W/m-K | 1.16 - 1.39 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 255 °C | 491 °F | Deflection Temp at unknown load |
| Processing Properties | Metric | English | Comments |
| Cure Time | 60.0 - 120 min @Temperature 150 - 160 °C | 1.00 - 2.00 hour @Temperature 302 - 320 °F | |
| 60.0 - 240 min @Temperature 160 - 180 °C | 1.00 - 4.00 hour @Temperature 320 - 356 °F | optional | |
| Pot Life | 160 min @Temperature 100 °C | 160 min @Temperature 212 °F | |
| Shelf Life | 5.00 - 8.00 Month | 5.00 - 8.00 Month | |